Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.20mm | | 1.1to1.3 | % |
| Modeling Shrinkage | MD:3.20mm | | 1.1to1.3 | % |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 31.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield,23°C | ISO527-2 | 66.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 5.3 | % |
| Tensile Modulus | 23°C | ISO527-2 | 2500 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2500 | Mpa |
| Flexural Stress | 23°C | ISO178 | 104 | Mpa |
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 42 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 185 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 105 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | 5E+14 | ohms |
| Volume Resistivity | | IEC60093 | 1E+16 | ohms·cm |
| Dissipation Factor? | 100Hz | IEC60250 | 4E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 9.4E-03 | |
| Dielectric Strength | 1.00mm | IEC60243-1 | 30 | KV/mm |
| Dielectric Strength | 3.00mm | IEC60243-1 | 17 | KV/mm |
| Relative Permittivity | 100Hz | IEC60250 | 3.30 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.20 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.