Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD:3.20mm | | 1.1to1.3 | % |
| Modeling Shrinkage | MD:3.20mm | | 1.1to1.3 | % |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 115 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Nominal Tensile Strain at Break | 23°C | ISO527-2 | 47 | % |
| Flexural Stress | 23°C | ISO178 | 93.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 62.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2 | 4.8 | % |
| Tensile Modulus | 23°C | ISO527-2 | 2600 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2400 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 165 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | 7E+14 | ohms |
| Volume Resistivity | | IEC60093 | 2E+15 | ohms·cm |
| Dielectric Strength | 1.00mm | IEC60243-1 | 33 | KV/mm |
| Dielectric Strength | 3.00mm | IEC60243-1 | 18 | KV/mm |
| Relative Permittivity | 100Hz | IEC60250 | 3.40 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.20 | |
| Dissipation Factor? | 100Hz | IEC60250 | 5E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.012 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.