PPO/PA NORYL GTX™ GTX678-74709 SABIC INNOVATIVE US
181
- Unit Price:
- $4756 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 31MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Hydrolysis resistance High temperature resistan Dimensional stability High mobility
- Application Areas:Electrical applications Industrial machinery
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 1.3到1.5 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 4.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.50 | % | |
| Melt mass flow rate | 300°C/5.0kg | ASTMD1238 | 7.8 | g/10min |
| Melt volume flow rate | 300°C/5.0kg | ISO1133 | 7.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending stress | --6,7 | ISO178 | 95.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 95.0 | Mpa | |
| Tensile strength | Yield4 | ASTMD638 | 58.0 | Mpa |
| Yield | ISO527-2/50 | 58.0 | Mpa | |
| Break4 | ASTMD638 | 52.0 | Mpa | |
| Break | ISO527-2/50 | 52.0 | Mpa | |
| Tensile modulus | --3 | ASTMD638 | 2900 | Mpa |
| -- | ISO527-2/1 | 2900 | Mpa | |
| elongation | Yield4 | ASTMD638 | 7.0 | % |
| Yield | ISO527-2/50 | 7.0 | % | |
| Break4 | ASTMD638 | 12 | % | |
| Break | ISO527-2/50 | 12 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2600 | Mpa |
| --6 | ISO178 | 2600 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 195 | °C |
| 0.45MPa,Unannealed,64.0mmSpan10 | ISO75-2/Bf | 191 | °C | |
| Vicat softening temperature | -- | ASTMD152511 | 198 | °C |
| -- | ISO306/B50 | 197 | °C | |
| -- | ISO306/B120 | 195 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 7.8E-05 | cm/cm/°C |
| MD:23to60°C | ISO11359-2 | 8.3E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 8E-05 | cm/cm/°C | |
| TD:23to60°C | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
| specific heat | ASTMC351 | 1400 | J/kg/°C | |
| thermal conductivity | ASTMC177 | 0.20 | W/m/K | |
| BallPressure Test | 125°C | IEC60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTMD257 | 4E+03 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| Impact strength of simply supported beam gap 8 | 23°C | ISO179/1eA | 12 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm,TestingbySABIC | UL94 | V-1 | |
| 2.0mm,TestingbySABIC | UL94 | V-05VB5VA | ||
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 800 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.