PPO/PA NORYL GTX™ GTX918W-14101 SABIC INNOVATIVE US

Unit Price:
$5055 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 3.20 mm	内部方法	1.3 到 1.6	%
Modeling Shrinkage	Modeling Shrinkage	Across Flow : 3.20 mm	内部方法	1.0 到 1.3	%
Moisture Absorption	Saturation, 23°C	ASTM D570	4.2	%
Melt Mass-Flow Rate	280°C/5.0 kg	ASTM D1238	45	g/10 min
Melt Volume flow Rate	280°C/1.2 kg	ISO 1133	5.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Elongation	Yield 3	ASTM D638	11	%
	Tensile Elongation	Yield	ISO 527-2/50	4.5	%
		Tensile Elongation	Break 3	ASTM D638	53	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	30	%
Flexural Modulus	50.0 mm Span 4	ASTM D790	2360	Mpa
Flexural Modulus	Flexural Modulus	-- 5	ISO 178	2200	Mpa
Tensile Strength	Yield 3	ASTM D638	62.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	60.0	Mpa
		Tensile Strength	Break 3	ASTM D638	57.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	55.0	Mpa
Flexural Stress	-- 5, 6	ISO 178	85.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 4	ASTM D790	98.0	Mpa
Tensile Modulus		ASTM D638	810	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Thermal Conductivity		ASTM C177	0.25	W/m/K
Vicat Softening Temperature	--	ASTM D152510	242	°C
	Vicat Softening Temperature	--	ISO 306/A50	245	°C
		Vicat Softening Temperature	--	ISO 306/B50	190	°C
		Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/B120	195	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	6.5E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 23 to 60°C	ISO 11359-2	8.0E-5	cm/cm/°C
		Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	6.8E-5	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 60°C	ISO 11359-2	8.0E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	188	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9	ISO 75-2/Be	185	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	148	°C

Injection	Test Result	Unit
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	30 到 50	%
Rear Temperature	255 到 295	°C
Middle Temperature	260 到 295	°C
Front Temperature	265 到 295	°C
Nozzle Temperature	270 到 295	°C
Back Pressure	0.300 到 1.40	Mpa
Screw Speed	20 到 100	rpm
Vent Depth	0.013 到 0.038	mm
Drying Temperature	95 到 105	°C
Suggested Max Moisture	0.070	%
Processing (Melt) Temp	270 到 295	°C
Mold Temperature	65 到 95	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	20	kJ/m²
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	40.0	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.