PPO/PA NORYL GTX™ GTX830 95202 SABIC INNOVATIVE US
101
- Unit Price:
- $9116 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:dimensional stability High temperature resistan Hydrolysis resistance
- Application Areas:Electrical applications Industrial machinery
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.20 到 0.30 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.65 到 0.85 | % | |
| Water absorption rate | 24 hr, 50% RH | ASTM D570 | 0.50 | % |
| Equilibrium, 50% RH | ASTM D570 | 1.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | Break | ASTM D638 | 7.0 | % |
| Bending modulus | 100 mm Span | ASTM D790 | 8580 | Mpa |
| bending strength | Yield, 100 mm Span | ASTM D790 | 248 | Mpa |
| Tensile strength 2 | Yield | ASTM D638 | 151 | Mpa |
| Break | ASTM D638 | 158 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTM D15255 | 248 | °C | |
| Linear coefficient of thermal expansion - flow | -20 to 150°C | ASTM E831 | 2.0E-5 到 3.1E-5 | cm/cm/°C |
| RTI | UL 746 | 50.0 | °C | |
| RTI Imp | UL 746 | 50.0 | °C | |
| RTI Elec | UL 746 | 50.0 | °C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 254 | °C |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 240 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 2 | ||
| High arc combustion index (HAI) 7 | UL 746 | PLC 2 | ||
| Hot wire ignition (HWI) | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 1 | ||
| Arc resistance 6 | ASTM D495 | PLC 6 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 50 | % | ||
| Temperature at the rear of the barrel | 265 到 305 | °C | ||
| Temperature in the middle of the barrel | 270 到 305 | °C | ||
| Temperature at the front of the material cylinder | 275 到 305 | °C | ||
| Spray nozzle temperature | 280 到 305 | °C | ||
| Back pressure | 0.300 到 1.40 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.013 到 0.038 | mm | ||
| drying temperature | 95 到 105 | °C | ||
| Suggested maximum moisture content | 0.070 | % | ||
| Processing (melt) temperature | 280 到 305 | °C | ||
| Mold temperature | 75 到 120 | °C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTM D785 | 120 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.