PPO/PA NORYL GTX™ GTX675 SABIC INNOVATIVE US
134
- Unit Price:
- $5252 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility dimensional stability High temperature resistan Hydrolysis resistance
- Application Areas:Electrical applications Industrial machinery
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 1.3到1.5 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 4.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.40 | % | |
| Melt Mass-Flow Rate | 300°C/5.0kg | ASTMD1238 | 7.8 | g/10min |
| Melt Volume flow Rate | 300°C/5.0kg | ISO1133 | 7.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | --5,6 | ISO178 | 103 | Mpa |
| Yield,50.0mmSpan4 | ASTMD790 | 100 | Mpa | |
| Tensile Strength | Yield3 | ASTMD638 | 65.0 | Mpa |
| Yield | ISO527-2/50 | 66.0 | Mpa | |
| Break3 | ASTMD638 | 63.0 | Mpa | |
| Break | ISO527-2/50 | 64.0 | Mpa | |
| Tensile Modulus | --2 | ASTMD638 | 2420 | Mpa |
| -- | ISO527-2/1 | 2670 | Mpa | |
| Tensile Elongation | Break3 | ASTMD638 | 6.1 | % |
| Break | ISO527-2/50 | 7.1 | % | |
| Yield3 | ASTMD638 | 3.8 | % | |
| Yield | ISO527-2/50 | 4.0 | % | |
| Flexural Modulus | 50.0mmSpan4 | ASTMD790 | 2520 | Mpa |
| --5 | ISO178 | 2470 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 187 | °C |
| 0.45MPa,Unannealed,64.0mmSpan9 | ISO75-2/Bf | 184 | °C | |
| Vicat Softening Temperature | -- | ASTMD152510,ISO306/B5010 | 197 | °C |
| -- | ISO306/B120 | 198 | °C | |
| Linear thermal expansion coefficient | TD:23to60°C | ISO11359-2 | 8.6E-05 | cm/cm/°C |
| MD:-40to40°C | ASTME831 | 7.6E-05 | cm/cm/°C | |
| MD:23to60°C | ISO11359-2 | 8.1E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 7.8E-05 | cm/cm/°C | |
| Ball PressureTest | 125°C | IEC60695-10-2 | 通过 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume Resistivity | 内部方法 | 1.0E+3到1.0E+4 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 5.00 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 12 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.