PPO/PA NORYL GTX™ GTX918W-71967 SABIC INNOVATIVE US
178
- Unit Price:
- $4420 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Aging resistance High temperature resistan
- Application Areas:Electronic communication household electrical appl Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 1.3 到 1.6 | % |
| Across Flow : 3.20 mm | 内部方法 | 1.0 到 1.3 | % | |
| Water absorption rate | Saturation, 23°C | ASTM D570 | 4.2 | % |
| Melt flow rate | 280°C/5.0 kg | ASTM D1238 | 45 | g/10 min |
| Molten Volume Flow Rate (MVR) | 280°C/1.2 kg | ISO 1133 | 5.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | Yield 3 | ASTM D638 | 11 | % |
| Yield | ISO 527-2/50 | 4.5 | % | |
| Break 3 | ASTM D638 | 53 | % | |
| Break | ISO 527-2/50 | 30 | % | |
| Bending modulus | 50.0 mm Span 4 | ASTM D790 | 2360 | Mpa |
| -- 5 | ISO 178 | 2200 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 62.0 | Mpa |
| Yield | ISO 527-2/50 | 60.0 | Mpa | |
| Break 3 | ASTM D638 | 57.0 | Mpa | |
| Break | ISO 527-2/50 | 55.0 | Mpa | |
| Bending stress | -- 5, 6 | ISO 178 | 85.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 98.0 | Mpa | |
| Tensile modulus 2 | ASTM D638 | 810 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| thermal conductivity | ASTM C177 | 0.25 | W/m/K | |
| Vicat softening temperature | -- | ASTM D152510 | 242 | °C |
| -- | ISO 306/A50 | 245 | °C | |
| -- | ISO 306/B50 | 190 | °C | |
| -- | ISO 306/B120 | 195 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ASTM E831 | 6.5E-5 | cm/cm/°C |
| Flow : 23 to 60°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| Across Flow : -40 to 40°C | ASTM E831 | 6.8E-5 | cm/cm/°C | |
| Across Flow : 23 to 60°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 188 | °C |
| 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 9 | ISO 75-2/Be | 185 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 148 | °C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying time | 3.0 到 4.0 | hr | ||
| Suggested injection volume | 30 到 50 | % | ||
| Temperature at the rear of the barrel | 255 到 295 | °C | ||
| Temperature in the middle of the barrel | 260 到 295 | °C | ||
| Temperature at the front of the material cylinder | 265 到 295 | °C | ||
| Spray nozzle temperature | 270 到 295 | °C | ||
| Back pressure | 0.300 到 1.40 | Mpa | ||
| Screw speed | 20 到 100 | rpm | ||
| Exhaust hole depth | 0.013 到 0.038 | mm | ||
| drying temperature | 95 到 105 | °C | ||
| Suggested maximum moisture content | 0.070 | % | ||
| Processing (melt) temperature | 270 到 295 | °C | ||
| Mold temperature | 65 到 95 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 10 | kJ/m² |
| 23°C | ISO 179/1eA | 20 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C, Energy at Peak | ASTM D3763 | 40.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.