PPO/PA NORYL GTX™ GTX900-74701 SABIC INNOVATIVE US
184
- Unit Price:
- $5071 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High temperature resistan
- Application Areas:For external use in autom
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD2 | 内部方法 | 1.6到2.0 | % |
| MD:3.20mm | 内部方法 | 1.4到1.7 | % | |
| TD:3.20mm | 内部方法 | 1.1到1.4 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 3.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.2 | % | |
| Melt mass flow rate | 280°C/5.0kg | ASTMD1238 | 13 | g/10min |
| Melt volume flow rate | 280°C/5.0kg | ISO1133 | 13.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield4 | ASTMD638 | 65.0 | Mpa |
| Yield | ISO527-2/50 | 65.0 | Mpa | |
| Break4 | ASTMD638 | 55.0 | Mpa | |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Bending stress | --6,7 | ISO178 | 90.0 | Mpa |
| Yield,50.0mmSpan5 | ASTMD790 | 95.0 | Mpa | |
| Tensile modulus | --3 | ASTMD638 | 2300 | Mpa |
| -- | ISO527-2/1 | 2400 | Mpa | |
| elongation | Yield4 | ASTMD638 | 5.0 | % |
| Yield | ISO527-2/50 | 4.5 | % | |
| Break4 | ASTMD638 | 60 | % | |
| Break | ISO527-2/50 | 25 | % | |
| Bending modulus | 50.0mmSpan5 | ASTMD790 | 2350 | Mpa |
| --6 | ISO178 | 2200 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 190 | °C |
| 0.45MPa,Unannealed,100mmSpan10 | ISO75-2/Be | 190 | °C | |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 7.5E-05 | cm/cm/°C |
| MD:23to60°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 8.5E-05 | cm/cm/°C | |
| TD:23to60°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| Vicat softening temperature | -- | ASTM D-596 | 205 | °C |
| -- | ISO306/A50 | 250 | °C | |
| -- | ISO306/B50 | 200 | °C | |
| thermal conductivity | ISO8302 | 0.23 | W/m/K | |
| BallPressure Test | 125°C | IEC60695-10-2 | 通过 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 60.0 | J |
| Impact strength of simply supported beam gap 8 | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 20 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 85.0 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.