Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 0.70到1.3 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.10到0.40 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break,23°C | ISO527-2 | 80.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 2.8 | % |
Tensile Modulus | 23°C | ISO527-2 | 5800 | Mpa |
Flexural Modulus | 23°C | ISO178 | 4200 | Mpa |
Flexural Stress | 23°C | ISO178 | 110 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 150 | °C |
Melting temperature | | ISO11357-3 | 225 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+13 | ohms |
Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
Dielectric Strength | 2.00mm | IEC60243-1 | 23 | KV/mm |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Viscosity | 260°C | ISO11443 | 185 | Pa·s |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.