Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 1.1 | g/10min |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 1.1 | g/10min |
| IonType | | | Zinc | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break,23°C | ISO527-2 | 25.5 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 410 | % |
| Taber Abrasion Resistance | | ASTMD1630 | 290 | |
| Tensile Elongation | Break,23°C | ASTMD638 | 410 | % |
| Flexural Modulus | -20°C | ASTMD790 | 655 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 260 | Mpa |
| Tensile Strength | Break,23°C | ASTMD638 | 25.5 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD1525 | 74.0 | °C |
| Vicat Softening Temperature | | ISO306 | 74.0 | °C |
| Melting temperature (DSC) | | ISO3146 | 96.0 | °C |
| Freezing Point | -- | ASTMD3418 | 76 | °C |
| Freezing Point | -- | ISO3146 | 76 | °C |
| Peak Melting Temperature | | ASTMD3418 | 96.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Impact Strength | -40°C | ASTMD1822 | 1030 | kJ/m² |
| Tensile Impact Strength | 23°C | ASTMD1822 | 1190 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D | ASTMD2240 | 60 | |
| Shore Hardness | Shore D | ISO868 | 60 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 6350µm | ASTMD1003 | 26 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.