PVDF SOLEF® 20810-20 SOLVAY USA
43
- Unit Price:
- $13847 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ISO 1183 | 1.78 | g/cm³ | |
| Modeling Shrinkage (Flow) | ASTM D995 | 2 | % | |
| Modeling Shrinkage (Across Flow) | ASTM D995 | 3 | % | |
| Moisture Absorption (23°C 24hr) | ISO 62 | 0.04 | % | |
| Melt Mass-Flow Rate (230°C 2.16kg) | ASTM D1238 | 2 | g/10min | |
| Melt Volume flow Rate (230°C 5kg) | ASTM D1238 | 6 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus (23°C 1.0mm/min) | ASTM D638 | 420 | Mpa | |
| Tensile Strength (23°C 50mm/min) | ASTM D638 | 40 | Mpa | |
| Tensile Strength (Yield 23°C) | ASTM D638 | 16.5 | Mpa | |
| Tensile Elongation (23°C) | ASTM D638 | 675 | % | |
| Tensile Elongation (Yield, 23°C, 50mm/min) | ASTM D638 | 13.5 | % | |
| Flexural Strength (23°C) | ASTM D790 | 40 | Mpa | |
| Flexural Modulus (23°C) | ASTM D790 | 400 | Mpa | |
| Notched Izod Impact Strength (23℃) | ASTM D256 | 180 | J/m | |
| Coefficient of Friction (Dynamic) | ASTM D3702 | 0.25 | ||
| Coefficient of Friction (Static) | ASTM D3702 | 0.3 | ||
| Taber Abrasion Resistance | 10 | mg/1000cy |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load (Annealed 4.0mm) | ASTM D648 | 62 | °C | |
| ASTM D648 | 40 | °C | ||
| Vicat Softening Temperature | ISO 306 | 120 | °C | |
| Melting Temperature | ASTM D3418 | 135 | °C | |
| Glass Transition Temperature | -29 | °C | ||
| Brittleness Temperature | ASTM D746 | -22 | °C | |
| Thermal Conductivity | JIS R2618 | 0.18 | W/(m·K) | |
| Specific Heat | 1200 | J/(kg·°C) | ||
| Specific Heat ( 100°C) | 1600 | J/(kg·°C) | ||
| Peak Crystallization Temperature | 92 | |||
| Peak Melting Temperature | 23 | J/g | ||
| 24 | J/g |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTM D257 | 100000000000000 | Ω | |
| Oxygen Index | ASTM D2863 | 54.5 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| hardness | 测试标准 | 数据 | 单位 | |
| Shore Hardness (Shore D) | ASTM D2240 | 60 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.