PC/PET XYLEX™ XL1339 SABIC INNOVATIVE US
88
- Unit Price:
- $3744 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High heat resistance
- Application Areas:Electronic and electrical Automotive components
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Volume flow Rate | 265°C/1.2 kg | ISO 1133 | 4.00 | cm3/10min |
| Modeling Shrinkage | Flow | 内部方法 | 0.50 到 0.80 | % |
| Across Flow | 内部方法 | 0.50 到 0.80 | % | |
| Moisture Absorption | 24 hr | ASTM D570 | 0.10 | % |
| Equilibrium, 23°C | ASTM D570 | 0.70 | % | |
| Equilibrium, 50% RH | ASTM D570 | 0.20 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ASTM D638 | 2090 | Mpa | |
| Tensile Strength | Yield 3 | ASTM D638 | 49.0 | Mpa |
| Yield | ISO 527-2/50 | 55.0 | Mpa | |
| Break 3 | ASTM D638 | 49.0 | Mpa | |
| Break | ISO 527-2/50 | 40.0 | Mpa | |
| Tensile Elongation | Yield 3 | ASTM D638 | 5.0 | % |
| Yield | ISO 527-2/50 | 5.0 | % | |
| Break 3 | ASTM D638 | 110 | % | |
| Break | ISO 527-2/50 | 70 | % | |
| Flexural Modulus | 50.0 mm Span 4 | ASTM D790 | 2090 | Mpa |
| -- 5 | ISO 178 | 2200 | Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 80.0 | Mpa |
| Yield, 50.0 mm Span 4 | ASTM D790 | 94.0 | Mpa | |
| Poisson Ratio | ASTM E132 | 0.40 | ||
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 Wheel | ASTM D1044 | 16.0 | mg |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Be | 125 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span | ISO 75-2/Ae | 105 | °C | |
| Vicat Softening Temperature | -- | ISO 306/A50 | 140 | °C |
| -- | ISO 306/B50 | 130 | °C | |
| -- | ISO 306/B120 | 135 | °C | |
| Linear thermal expansion coefficient | Flow : -30 to 30°C | ASTM D696 | 7.6E-5 | cm/cm/°C |
| Across Flow : -30 to 30°C | ASTM D696 | 7.9E-5 | cm/cm/°C | |
| Thermal Conductivity | ASTM C177 | 0.18 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | ASTM D257 | > 1.0E+15 | ohms | |
| Volume Resistivity | ASTM D257 | > 1.0E+14 | ohms·cm | |
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 17 | KV/mm |
| Dielectric Constant | 60 Hz | ASTM D150 | 3.30 | |
| 50 kHz | ASTM D150 | 3.30 | ||
| 1 MHz | ASTM D150 | 3.10 | ||
| Dissipation Factor? | 50 Hz | ASTM D150 | 2.0E-3 | |
| 60 Hz | ASTM D150 | 2.0E-3 | ||
| 1 MHz | ASTM D150 | 0.020 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 110 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Max Moisture | 0.020 | % | ||
| Suggested Shot Size | 50 到 80 | % | ||
| Rear Temperature | 245 到 265 | °C | ||
| Middle Temperature | 250 到 270 | °C | ||
| Front Temperature | 255 到 275 | °C | ||
| Nozzle Temperature | 255 到 270 | °C | ||
| Processing (Melt) Temp | 260 到 275 | °C | ||
| Mold Temperature | 65 到 90 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 50 到 80 | rpm | ||
| Vent Depth | 0.013 到 0.020 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 35 | kJ/m² |
| 23°C | ISO 179/1eA | 45 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 无断裂 | |
| 23°C | ISO 179/1eU | 无断裂 | ||
| Unnotched Izod Impact Strength | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.