PC/PET XYLEX™ X7300 NA9A002 SABIC INNOVATIVE NANSHA
141
- Unit Price:
- $3744 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 12MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance High mobility
- Application Areas:Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| TD：3.20mm | 内部方法 | 0.50to0.70 | % | |
| Melt Mass-Flow Rate | 265°C/2.16kg | ASTMD1238 | 21 | g/10min |
| Melt Volume flow Rate | 265°C/2.16kg | ISO1133 | 21.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break | ASTMD638 | 150 | % |
| Flexural Modulus | ISO178 | 2000 | Mpa | |
| Flexural Strength | ISO178 | 71.0 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 55.0 | Mpa |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 5.0 | % |
| Break | ISO527-2/50 | >150 | % | |
| Tensile Modulus | ISO527-2/1 | 1900 | Mpa | |
| Tensile Elongation | Yield | ASTMD638 | 5.0 | % |
| Tensile Modulus | ASTMD638 | 1840 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 49.0 | Mpa |
| Break | ASTMD638 | 52.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 1940 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 83.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 102 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 88.0 | °C | |
| Vicat Softening Temperature | ASTMD15259 | 108 | °C | |
| ISO306/B120 | 106 | °C | ||
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 1.2E-04 | cm/cm/°C |
| MD：23to60°C | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.1E-04 | cm/cm/°C | |
| TD：23to60°C | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,100mmSpan | ISO75-2/Ae | 90.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 9.0 | kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 95.0 | J |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance | 2540µm | ASTMD1003 | 88.0 | % |
| Haze | 2540µm | ASTMD1003 | 2.0 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.