PC/PET XYLEX™ HX7509HP SABIC INNOVATIVE US

Unit Price:
$3794 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
12MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD:3.20mm	内部方法	0.40到0.60	%
Modeling Shrinkage	Modeling Shrinkage	TD:3.20mm	内部方法	0.50到0.70	%
Moisture Absorption	Saturation,23°C	ISO62	0.12	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.050	%
Melt Mass-Flow Rate	265°C/2.16kg	ASTMD1238	12	g/10min
Melt Volume flow Rate	265°C/2.16kg	ISO1133	11.5	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strength	Yield4	ASTMD638	60.0	Mpa
	Tensile Strength	Yield	ISO527-2/50	60.0	Mpa
		Tensile Strength	Break4	ASTMD638	63.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO527-2/50	62.0	Mpa
Flexural Stress	--6,7	ISO178	92.0	Mpa
Flexural Stress	Flexural Stress	Yield,50.0mmSpan5	ASTMD790	95.0	Mpa
Tensile Modulus	--3	ASTMD638	2150	Mpa
Tensile Modulus	Tensile Modulus	--	ISO527-2/1	2300	Mpa
Tensile Elongation	Break	ISO527-2/50	130	%
	Tensile Elongation	Yield4	ASTMD638	6.3	%
		Tensile Elongation	Yield	ISO527-2/50	5.8	%
		Tensile Elongation	Tensile Elongation	Break4	ASTMD638	140	%
Flexural Modulus	50.0mmSpan5	ASTMD790	2300	Mpa
Flexural Modulus	Flexural Modulus	--6	ISO178	2260	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	119	°C
	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	106	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,64.0mmSpan10	ISO75-2/Af	108	°C
Linear thermal expansion coefficient	TD:-40to40°C	ISO11359-2	6.8E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD:-40to40°C	ASTME831	1E-04	cm/cm/°C
		Linear thermal expansion coefficient	MD:-40to40°C	ISO11359-2	6.8E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD:-40to40°C	ASTME831	1E-04	cm/cm/°C
Vicat Softening Temperature	--	ASTM D-596	126	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B50	125	°C
Thermal Conductivity		ISO8302	0.23	W/m/K

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	77.0	J
Charpy Notched Impact Strength	23°C	ISO179/1eA	10	kJ/m²

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance	2540µm	ASTMD1003	88.0	%
Haze	2540µm	ASTMD1003	2.0	%

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.