Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO2577 | 0.60to0.80 | % |
Modeling Shrinkage | MD | ISO2577 | 0.60to0.80 | % |
Moisture Absorption | 饱和,23°C | ISO62 | 0.50 | % |
Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.20 | % |
Melt Volume flow Rate | 270°C/5.0kg | ISO1133 | 20.0 | cm3/10min |
Density | 23°C | ISO1183 | 1.22 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | 23°C | ISO527-2/50 | 100 | % |
Tensile Stress | 屈服,23°C | ISO527-2/50 | 59.0 | Mpa |
Tensile Stress | 断裂,23°C | ISO527-2/50 | 64.0 | Mpa |
Tensile Strain | 屈服,23°C | ISO527-2/50 | 5.5 | % |
Tensile Modulus | 23°C | ISO527-2/1 | 2400 | Mpa |
Flexural Modulus | 23°C | ISO178 | 2350 | Mpa |
Flexural Stress | 23°C | ISO178 | 88.0 | Mpa |
Flexural Stress | 3.5%Strain,23°C | ISO178 | 71.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 131 | °C |
Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 109 | °C |
Linear thermal expansion coefficient | MD:23到55°C | ISO11359-2 | 7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
Vicat Softening Temperature | | ISO306/B120 | 142 | °C |
ThermalConductivity | 23°C | ISO8302 | 0.20 | W/m/K |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | 23°C | IEC60093 | 1E+16 | ohms·cm |
Dielectric Strength | 23°C,1.00mm | IEC60243-1 | 34 | KV/mm |
Comparative Tracking Index | 解决方案A | IEC60112 | 375 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | -30°C | ISO7391 | 10 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO7391 | 60 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.