| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD1 | ISO2577 | 0.65 | % |
| Modeling Shrinkage | TD:90°C,1hr | ISO2577 | 0.10 | % |
| Modeling Shrinkage | MD2 | ISO2577 | 0.65 | % |
| Modeling Shrinkage | MD:90°C,1hr | ISO2577 | 0.10 | % |
| Melt Volume flow Rate | 270°C/5.0kg | ISO1133 | 49.0 | cm3/10min |
| Density / Specific Gravity | 23°C | ISO1183 | 1.24 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 23°C | ISO527-2/1 | 2600 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2/50 | 70.0 | Mpa |
| Tensile Stress | Break,23°C | ISO527-2/50 | 54.0 | Mpa |
| Tensile Strain | Yield,23°C | ISO527-2/50 | 5.5 | % |
| Tensile Strain | Break,23°C | ISO527-2/50 | 110 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO306/B120 | 140 | °C |
| RTI | | UL746 | 75.0 | °C |
| RTIElec | | UL746 | 75.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 75.0 | °C |
| 0.45MPa, Unannealed | | ISO75-2/B | 128 | °C |
| 1.8MPa, Unannealed | | ISO75-2/A | 108 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/A | 6.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/A | 7.0 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.50mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.