Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD:3.20mm | | 0.60to0.80 | % |
Modeling Shrinkage | MD:3.20mm | | 0.60to0.80 | % |
Moisture Absorption | Saturation,23°C | ISO62 | 0.20 | % |
Melt Mass-Flow Rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 9.20 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2 | 140 | % |
Flexural Stress | | ISO178 | 78.0 | Mpa |
Tensile Stress | Yield | ISO527-2 | 50.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 5.9 | % |
Tensile Modulus | | ISO527-2 | 2100 | Mpa |
Flexural Modulus | | ISO178 | 2000 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 132 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 112 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 8E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 9.6E-05 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 100Hz | IEC60250 | 8.1E-03 | |
Dissipation Factor? | 1MHz | IEC60250 | 0.023 | |
Dielectric Strength | 2.00mm | IEC60243-1 | 24 | KV/mm |
Dielectric Strength | 3.00mm | IEC60243-1 | 18 | KV/mm |
Relative Permittivity | 100Hz | IEC60250 | 4.40 | |
Relative Permittivity | 1MHz | IEC60250 | 3.50 | |
Surface Resistivity | | IEC60093 | 7E+11 | ohms |
Volume Resistivity | | IEC60093 | 3E+13 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.