PC/PET XYLEX™ 5220U GY3A500 SABIC INNOVATIVE US
92
- Unit Price:
- $3407 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant High heat resistance
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific Volume | ASTM D792 | 0.830 | cm³/g | |
| Melt Mass-Flow Rate | 250°C/5.0 kg | ISO 1133 | 16 | g/10 min |
| Melt Volume flow Rate | 250°C/5.0 kg | ISO 1133 | 15.0 | cm3/10min |
| Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.80 到 1.0 | % |
| Across Flow 2 | 内部方法 | 0.80 到 1.0 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.50 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % | |
| Outdoor Suitability | UL 746C | f2 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | -- 3 | ASTM D638 | 2250 | Mpa |
| -- 4 | ASTM D638 | 2250 | Mpa | |
| -- | ISO 527-2/1 | 2050 | Mpa | |
| Tensile Strength | Yield 5 | ASTM D638 | 53.0 | Mpa |
| Yield | ISO 527-2/50 | 50.0 | Mpa | |
| Break 5 | ASTM D638 | 51.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa | |
| Tensile Elongation | Yield 5 | ASTM D638 | 4.0 | % |
| Yield | ISO 527-2/50 | 4.0 | % | |
| Break 5 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/50 | 120 | % | |
| Flexural Modulus | 50.0 mm Span 6 | ASTM D790 | 2030 | Mpa |
| -- 7 | ISO 178 | 2000 | Mpa | |
| Flexural Stress | -- 7, 8 | ISO 178 | 80.0 | Mpa |
| Yield, 50.0 mm Span 6 | ASTM D790 | 84.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 107 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 84.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 99.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | ISO 75-2/Af | 75.0 | °C | |
| Vicat Softening Temperature | -- | ASTM D152511 | 122 | °C |
| -- | ISO 306/B50 | 120 | °C | |
| -- | ISO 306/B120 | 125 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 9.5E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 9.0E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | 75.0 | °C | |
| RTI Imp | UL 746 | 75.0 | °C | |
| RTI | UL 746 | 75.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Arc Resistance | ASTM D495 | PLC 5 | ||
| Comparative Tracking Index | UL 746 | PLC 1 | ||
| High Amp Arc Ignition | UL 746 | PLC 0 | ||
| High Voltage Arc Tracking Rate | UL 746 | PLC 0 | ||
| Hot-wire Ignition | UL 746 | PLC 3 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 110 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Max Moisture | 0.020 | % | ||
| Suggested Shot Size | 50 到 80 | % | ||
| Rear Temperature | 245 到 265 | °C | ||
| Middle Temperature | 250 到 270 | °C | ||
| Front Temperature | 255 到 275 | °C | ||
| Nozzle Temperature | 255 到 270 | °C | ||
| Processing (Melt) Temp | 260 到 275 | °C | ||
| Mold Temperature | 65 到 90 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 50 到 80 | rpm | ||
| Vent Depth | 0.013 到 0.020 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 60.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.