Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 0.93 | |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.002 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238 | 7.0 | g/10min |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 7.0 | g/10min |
Acrylic Acid Content | | | 7.0 | wt% |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength(Break) | TD | MPa | ASTM D-882 | |
Tensile Strength(Break) | MD | MPa | ASTM D-882 | |
Secant Modulus (1%Secant) | MD | MPa | ASTM D-882 | 170 |
Secant Modulus (1%Secant) | TD | MPa | ASTM D-882 | 175 |
Tensile Elongation?(Break) | MD | % | ASTM D-882 | |
Tensile Elongation?(Break) | TD | % | ASTM D-882 | 560 |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 500 | % |
Tensile Modulus | | ASTM D638/ISO 527 | 100 | kg/cm²(MPa)[Lb/in²] |
Tensile Strength | | ASTM D638/ISO 527 | 28.5 | kg/cm²(MPa)[Lb/in²] |
Rockwell Hardness | | ASTM D785 | 80 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ℃ | ASTM D-1525 | 84 |
Vicat Softening Temperature | | ℃ | ISO 306 | 84 |
Vicat Softening Temperature | | ASTMD1525 | 84.0 | °C |
Vicat Softening Temperature | | ISO306 | 84.0 | °C |
Melting temperature | | ℃ | DSC | 102 |
Melting temperature (DSC) | | ISO3146 | 102 | °C |
Freezing Point | -- | ISO3146 | 85 | °C |
Freezing Point | -- | ASTMD3418 | 85 | °C |
Peak Melting Temperature | | ASTMD3418 | 102 | °C |
Processing | Test Condition | Test Method | Test Result | Unit |
---|
Melt Temperature | | | 150 | °C |
Mold Temperature | | | 60 | °C |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Haze | | % | ASTM D-1003 | 3 |
Gloss | 20° | | ASTM D-2457 | |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 190℃/2.16kg | g/10min | ASTM D-1238 | |
Melt Mass-Flow Rate | 190℃/2.16kg | g/10min | ISO 1133 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.