EAA PRIMACOR™ 3460 DOW USA
204
- Unit Price:
- $3876 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 20 | g/10min |
| Content of comonomer 3 | 内部方法 | 9.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield,Compression Molded | ASTMD638,ISO527-2 | 7.24 | Mpa |
| Break,Compression Molded | ASTMD638,ISO527-2 | 16.2 | Mpa | |
| elongation | Break,Compression Molded | ASTMD638,ISO527-2 | 580 | % |
| Tensile yield strength | Compression Molded | MPa | ASTM D-638 | 7.24 |
| Compression Molded | MPa | ISO 527-2 | 7.24 | |
| Tensile fracture strength | Compression Molded | MPa | ASTM D-638 | 16.2 |
| Compression Molded | MPa | ISO 527-2 | 16.2 | |
| Tensile strain at break | Compression Molded | % | ASTM D-638 | 580 |
| Compression Molded | MPa | ISO 527-2 | 580 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ℃ | ASTM D-1525 | 72.2 | |
| ℃ | ISO 306 | 72.2 | ||
| Melting temperature | ℃ | Internal Method | ||
| Vicat softening temperature | ASTMD1525,ISO306 | 72.2 | °C | |
| Melting temperature (DSC) | 内部方法 | 95.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Initial sealing temperature 4 | 内部方法 | 85.0 | °C | |
| Water vapor permeability | 38°C,90%RH | DIN53122/2 | 0.44 | g·mm/m²/atm/24hr |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | |
| 190℃/2.16kg | g/10min | ISO 1133 | ||
| Monomer content | % | Internal Method |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Sealing starting temperature | ℃ | Internal Method | 85 | |
| Water vapor transmission rate | 38℃，90% RH | g·mm/m | DIN 53122/2 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.