Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 9.0 | g/10min |
| monomer Content | 内部方法 | 6.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Elongation | Break,Compression Molded | ASTMD638,ISO527-2 | 630 | % |
| Tensile Strength(Break) | Compression Molded | MPa | ASTM D-638 | |
| Compression Molded | MPa | ISO 527-2 | ||
| Tensile Strength | Yield,Compression Molded | ASTMD638,ISO527-2 | 7.89 | Mpa |
| Break,Compression Molded | ASTMD638,ISO527-2 | 17.2 | Mpa | |
| Tensile Strength(Yield) | Compression Molded | MPa | ASTM D-638 | 7.89 |
| Compression Molded | MPa | ISO 527-2 | 7.89 | |
| Tensile Elongation?(Break) | Compression Molded | % | ISO 527-2 | |
| Compression Molded | % | ASTM D-638 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature (DSC) | 内部方法 | 101 | °C | |
| Melting temperature | ℃ | Internal Method | 101 | |
| Vicat Softening Temperature | ASTMD1525,ISO306 | 83.9 | °C | |
| Vicat Softening Temperature | ℃ | ASTM D-1525 | 83.9 | |
| ℃ | ISO 306 | 83.9 |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water Vapor Transmission Rate | 38°C,90%RH | DIN53122/2 | 0.40 | g·mm/m²/atm/24hr |
| Peak Melting Temperature | 内部方法 | 92.8 | °C |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | ℃ | 260-290 |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water Vapor Permeability | 38℃，90% RH | g·mm/m | DIN 53122/2 | |
| Sealing Initial Temperature | ℃ | Internal Method | 92.8 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| monomer Content | % | Internal Method | ||
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | |
| 190℃/2.16kg | g/10min | ISO 1133 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.