EAA PRIMACOR™ 3330 STYRON US
227
- Unit Price:
- $3383 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Heat sealing performance High toughness
- Application Areas:Food service sector
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238,ISO1133 | 5.8 | g/10min |
| Content of comonomer 3 | 内部方法 | 6.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| elongation | Break,Compression Molded | ASTMD638,ISO527-2 | 520 | % |
| Tensile fracture strength | Compression Molded | MPa | ISO 527-2 | 17.4 |
| Compression Molded | MPa | ASTM D-638 | 17.4 | |
| Tensile strength | Yield,Compression Molded | ASTMD638,ISO527-2 | 8.34 | Mpa |
| Break,Compression Molded | ASTMD638,ISO527-2 | 17.4 | Mpa | |
| Tensile yield strength | Compression Molded | MPa | ASTM D-638 | 8.34 |
| Compression Molded | MPa | ISO 527-2 | 8.34 | |
| Tensile strain at break | Compression Molded | % | ASTM D-638 | 520 |
| Compression Molded | % | ISO 527-2 | 520 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature (DSC) | 内部方法 | 100 | °C | |
| Vicat softening temperature | ASTMD1525,ISO306 | 85.0 | °C | |
| vicat softening point | ℃ | ASTM D-1525 | 85 | |
| ℃ | ISO 306 | 85 |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water vapor permeability | 38°C,90%RH | DIN53122/2 | 0.40 | g·mm/m²/atm/24hr |
| Initial sealing temperature 4 | 内部方法 | 92.8 | °C |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | ℃ | 260-290 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water vapor transmission rate | 38℃，90% RH | g·mm/m | DIN 53122/2 | |
| Sealing starting temperature | ℃ | Internal Method | 92.8 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Monomer content | % | Internal Method | ||
| Melt index | 190℃/2.16kg | g/10min | ASTM D-1238 | |
| 190℃/2.16kg | g/10min | ISO 1133 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.