EAA PRIMACOR™ 1321 STYRON US
224
- Unit Price:
- $3494 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Heat sealing performance Resistance to stress crac high strength High toughness
- Application Areas:Multi layer composite mat Food packaging Food service sector Food containers
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Content of comonomer 3 | 内部方法 | 6.5 | % | |
| Density/specific gravity | ASTMD792,ISO1183/A | 0.935 | g/cm³ | |
| g/cm³ | ASTM D-792 | 0.935 | ||
| g/cm³ | ISO 1183/A | 0.935 | ||
| Melt mass flow rate 2 | 190°C/2.16kg | ASTMD1238,ISO1133 | 2.6 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - Tested | um | 50.8 | ||
| Tensile yield strength | Compression Molded | MPa | ASTM D-638 | |
| Compression Molded | MPa | ISO 527-2/508 | ||
| Tensile strain at break | Compression Molded | % | ASTM D-638 | |
| Compression Molded | % | ISO 527-2/508 | ||
| Tensile yield strength (TD) | 50.8um | MPa | ISO 527-3 | 11.5 |
| 50.8um | MPa | ASTM D-882 | 11.1 | |
| Tensile yield strength (MD) | 50.8um | MPa | ISO 527-3 | 11.3 |
| 50.8um | MPa | ASTM D-882 | 11.3 | |
| Falling hammer impact | 50.8um | g | ASTM D-1709B | 410 |
| 50.8um | g | ISO 7765-1/B | 410 | |
| elongation | Break,Compression Molded | ISO527-2/508 | 640 | % |
| Break,Compression Molded4 | ASTMD638 | 640 | % | |
| Tensile strength | Break,Compression Molded | ISO527-2/508 | 20.1 | Mpa |
| Break,Compression Molded4 | ASTMD638 | 20.1 | Mpa | |
| Yield,Compression Molded | ISO527-2/508 | 10.0 | Mpa | |
| Yield,Compression Molded4 | ASTMD638 | 10.0 | Mpa | |
| Tensile fracture strength | Compression Molded | MPa | ISO 527-2/508 | 20.1 |
| Compression Molded | MPa | ASTM D-638 | 20.1 | |
| Tensile elongation at break (MD) | 50.8um | % | ASTM D-882 | |
| 50.8um | % | ISO 527-3 | ||
| Tensile elongation at break (TD) | 50.8um | % | ISO 527-3 | 510 |
| 50.8um | % | ASTM D-882 | 510 | |
| Elmendorf Tear Strength (TD) | 50.8um | g | ASTM D-1922 | 390 |
| 50.8um | N | ISO 6383-2 | 1700 | |
| Elmendorf Tear Strength (MD) | 50.8um | N | ISO 6383-2 | 1200 |
| 50.8um | g | ASTM D-1922 | 270 | |
| Tensile fracture strength (TD) | 50.8um | MPa | ISO 527-3 | 31.8 |
| 50.8um | MPa | ASTM D-882 | 31.8 | |
| Tensile strength at break (MD) | 50.8um | MPa | ASTM D-882 | 31.8 |
| 50.8um | MPa | ISO 527-3 | 31.8 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTMD1525,ISO306 | 88.9 | °C | |
| vicat softening point | ℃ | ASTM D-1525 | 88.9 | |
| ℃ | ISO 306 | 88.9 | ||
| Melting temperature | ℃ | DSC | 103 | |
| Melting temperature (DSC) | 内部方法 | 103 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elmondov tear strength 5 | TD:51µm | ASTMD1922 | 390 | g |
| MD:51µm | ISO6383-2 | 1200 | N | |
| TD:51µm | ISO6383-2 | 1700 | N | |
| MD:51µm | ASTMD1922 | 270 | g | |
| elongation | MD:Break,51μm | ASTMD882,ISO527-3 | 460 | % |
| TD:Break,51μm | ASTMD882,ISO527-3 | 510 | % | |
| Tensile strength | MD:Yield,51μm | ASTMD882 | 11.3 | Mpa |
| TD:Yield,51μm | ASTMD882 | 11.1 | Mpa | |
| MD:Yield,51μm | ISO527-3 | 11.3 | Mpa | |
| TD:Yield,51μm | ISO527-3 | 11.5 | Mpa | |
| MD:Break,51μm | ASTMD882,ISO527-3 | 31.8 | Mpa | |
| TD:Break,51μm | ASTMD882,ISO527-3 | 31.8 | Mpa | |
| Falling hammer impact | 51µm | ASTMD1709B,ISO7765-1/B | 410 | g |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | ℃ | 193 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 45°，50.8um | ASTM D-2457 | 76 | |
| 45°,50.8µm | ASTMD2457 | 76 | ||
| Haze | 50.8um | % | ASTM D-1003 | 3.7 |
| 50.8um | % | ISO 14782 | 3.7 | |
| 50.8µm | ISO14782 | 3.7 | % | |
| 50.8µm | ASTMD1003 | 3.7 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 190℃/2.16kg | g/10min | ASTM D-1238 | 2.6 |
| 190℃/2.16kg | g/10min | ISO 1133 | 2.6 | |
| Monomer content | % | Internal Method |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.