Technical Data Sheet
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 23℃ | MPa | ASTM D-1708 | 400-500 |
| Tensile Elongation?(Break) | 23℃ | % | ASTM D-1708 | ＞300 |
| Charpy Notched Impact Strength | | | ASTM D-3307 | No Break |
| Tensile Strength(Break) | 23℃ | MPa | ASTM D-1708 | >28 |
| Shore Hardness | Shore D | | ASTM D-2240 | 55-60 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Specific Heat | 23℃ | J/kg/℃ | DSC | 900-1100 |
| Coefficient of Linear Thermal Expansion (Flow) | | cm/cm/℃ | ASTM D-696 | 0.00012-0.0002 |
| Melting temperature | | ℃ | ASTM D-3307 | 265-275 |
| Peak Melting Temperature | | J/g | DSC | 16-24 |
| Peak Crystallization Temperature | | ℃ | ASTM D-3418 | 255-265 |
| Peak Crystallization Temperature | | J/g | DSC | 16-24 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | 23℃，50Hz | | ASTM D-150 | 2 |
| Dielectric Constant | 23℃，100000Hz | | ASTM D-150 | 2 |
| Volume Resistivity | | ohm·cm | ASTM D-257 | >1E+17 |
| Surface resistance | | ohms | ASTM D-257 | >1E+17 |
| Dissipation Factor? | 23℃，50Hz | | ASTM D-150 | 0.0005 |
| Dissipation Factor? | 23℃，100000Hz | | ASTM D-150 | 0.0005 |
| Dielectric Strength | 1mm | kV/mm | ASTM D-149 | 35-40 |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | % | ASTM D-1003 | |
| Flame Rating | | | UL 94 | V-0 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 372℃/5.0kg | g/10min | ASTM D-1238 | 4-8 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.