Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	TD：--3	内部方法	0.40to0.60	%
	Modeling Shrinkage	TD：--4	内部方法	0.50to1.0	%
		Modeling Shrinkage	TD：3.20mm	内部方法	0.50to1.0	%
			Modeling Shrinkage	MD：--2	内部方法	0.50to0.80	%
				Modeling Shrinkage	MD：--3	内部方法	0.30to0.50	%
					Modeling Shrinkage	MD：--4	内部方法	0.30to0.70	%
						Modeling Shrinkage	MD：3.20mm	内部方法	0.30to0.80	%
						Modeling Shrinkage	Modeling Shrinkage	TD：--5	内部方法	0.60to0.90	%
Moisture Absorption	24hr	ASTMD570	0.060	%
	Moisture Absorption	Saturation,23°C	ISO62	0.26	%
	Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.080	%
Melt Mass-Flow Rate	250°C/2.16kg	ASTMD1238	17	g/10min
Melt Volume flow Rate	250°C/2.16kg	ISO1133	13.0	cm3/10min
Specific Volume		ASTMD792	0.650	cm³/g

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Strain	Break	ASTMD638	3.0	%
Tensile Strain	Tensile Strain	Yield	ASTMD638	3.0	%
Flexural Modulus	50.0mmSpan	ASTMD790	7580	Mpa
Tensile Strength	Break	ASTMD638	120	Mpa
Tensile Strength	Tensile Strength	Yield	ASTMD638	120	Mpa
Flexural Strength	Break,50.0mmSpan	ASTMD790	189	Mpa
Flexural Modulus		ISO178	8500	Mpa
Flexural Modulus		ISO178	195	Mpa
Tensile Modulus		ASTMD638	9300	Mpa
Tensile Modulus		ISO527-2/1	9300	Mpa
Tensile Stress	Yield	ISO527-2/5	125	Mpa
Tensile Stress	Tensile Stress	Break	ISO527-2/5	125	Mpa
Tensile Strain	Yield	ISO527-2/5	2.0	%
Tensile Strain	Tensile Strain	Break	ISO527-2/5	2.0	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed,3.20mm	ASTMD648	220	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed,6.40mm	ASTMD648	216	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	203	°C
Vicat Softening Temperature		ASTMD152514	215	°C
	Vicat Softening Temperature	--	ISO306/A50	223	°C
		Vicat Softening Temperature	--	ISO306/B50	215	°C
		Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	215	°C
Linear thermal expansion coefficient	MD：-40to40°C	ASTME831	2.5E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD：-40to40°C	ISO11359-2	2.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD：-40to40°C	ASTME831	1.2E-04	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：-40to40°C	ISO11359-2	1.2E-04	cm/cm/°C
Heat Deflection Temperature	0.45MPa,Unannealed,64.0mmSpan	ISO75-2/Bf	217	°C
Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO75-2/Af	204	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	1.60mm,in Oil	ASTMD149	25	KV/mm
Dielectric Strength	Dielectric Strength	3.20mm,inAir	ASTMD149	19	KV/mm
Dielectric Constant	100Hz	ASTMD150	3.80
Dielectric Constant	Dielectric Constant	1MHz	ASTMD150	3.70
Volume Resistivity		ASTMD257	>3.2E+16	ohms·cm
Dissipation Factor?	100Hz	ASTMD150	2E-03
Dissipation Factor?	Dissipation Factor?	1MHz	ASTMD150	0.020

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	8.00	J
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	45	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	45	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	5.0	kJ/m²
Unnotched Izod Impact Strength	-30°C	ISO180/1U	45	kJ/m²
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C	ISO180/1U	45	kJ/m²
Notched Izod Impact Strength	-30°C	ISO180/1A	7.0	kJ/m²
Notched Izod Impact Strength	Notched Izod Impact Strength	23°C	ISO180/1A	8.0	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale	ASTMD785	118

Supplementary information	Test Condition	Test Method	Test Result	Unit
Filler Content		ASTMD229	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.