Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.11 | |
Modeling Shrinkage | | ASTM D955 | MD 0.4~0.7 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.01 | % |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | 内部方法 | 0.50to0.80 | % |
Modeling Shrinkage | MD | 内部方法 | 0.40to0.70 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.010 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO527-2 | 75.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 2.7 | % |
Flexural Stress | | ISO178 | 120 | Mpa |
Tensile Elongation?(Break) | | ASTM D638/ISO 527 | 2.7 | % |
Tensile Modulus | | ISO527-2 | 5400 | Mpa |
Tensile Strength | | ASTM D638/ISO 527 | 75 | kg/cm²(MPa)[Lb/in²] |
Rockwell Hardness | | ASTM D785 | 45 | |
Flexural Modulus | | ASTM D790/ISO 178 | 5 | kg/cm²(MPa)[Lb/in²] |
Flexural Modulus | | ISO178 | 5000 | Mpa |
Flexural Strength | | ASTM D790/ISO 178 | 120 | kg/cm²(MPa)[Lb/in²] |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | UL94 | HB/0.80 | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 260 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 140 | °C |
Linear expansion coefficient | | ASTM D696/ISO 11359 | MD 3 | mm/mm.℃ |
Linear thermal expansion coefficient | MD:-30to30°C | TMA | 3E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-30to30°C | TMA | 8.1E-05 | cm/cm/°C |
RTIElec | | UL746 | 50.0 | °C |
Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
RTIStr | | UL746 | 50.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dissipation Factor? | 1MHz | IEC60250 | <1.0E-3 | |
Dielectric Strength | | ASTMD149 | 45 | KV/mm |
Comparative Tracking Index | CTI)3 | IEC60112 | PLC0 | |
Dielectric Constant | 1MHz | IEC60250 | 2.80 | |
Arc Resistance | | ASTMD495 | PLC6 | |
Arc Resistance | | ASTM D495/IEC 60112 | 105 | |
Volume Resistivity | | ASTM D257/IEC 60093 | >1.0*10^16 | Ω.cm |
Volume Resistivity | | IEC60093 | >1.0E+16 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180 | 30 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 35 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | >0.8mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.