Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 0.70-0.90 | % |
| Modeling Shrinkage | Flow | ISO 294-4 | 0.15-0.30 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | | ISO 180 | 50.0 | KJ/m |
| Fracture strain | | ISO 527-2 | 1.9 | % |
| Tensile Stress (Yield) | | ISO 527-2 | 125 | Mpa |
| Flexural Modulus | | ISO 178 | 10400 | Mpa |
| Flexural Strength | | ISO 178 | 195 | Mpa |
| Charpy Notched Impact Strength | | ISO 179 | 9.00 | kJ/m² |
| Charpy Unnotched Impact Strength | | ISO 179 | 39.00 | KJ/m |
| IZOD Notch Impact Strength | | ISO 180 | 12.0 | KJ/m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame retardancy | 1.50mm | UL 94 | V-0 | |
| Deflection Temperature Under Load? | 1.80MPa，Unannealed | ISO 75-2/B | 245 | °C |
| RTI Str | 1.50mm | UL 746 | 120 | °C |
| RTI Imp | 1.50mm | UL 746 | 120 | °C |
| RTI Elec | 1.50mm | UL 746 | 125 | °C |
| Vicat Softening Temperature | | ISO 306 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dissipation Factor? | | IEC 60250 | 0.00200 | |
| Dielectric Constant | | IEC 60250 | 3.200 | |
| Volume Resistivity | | IEC 60093 | 1.3E+18 | ohm.cm |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Stauration，23℃ | ISO 62 | 0.090 | % |
| Density | | ISO 1183/B | 1.39 | g/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.