PC/PBT XENOY™ 5220U-7A1D007 SABIC INNOVATIVE SHANGHAI
97
- Unit Price:
- $2881 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 53MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:UV resistance Antichemical
- Application Areas:Electronic accessories
- Color:--
- Grade:UV resistant grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | Flow : 3.20 mm | 内部方法 | 0.80 到 1.0 | % |
| Across Flow 2 | 内部方法 | 0.80 到 1.0 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.50 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % | |
| Melt Mass-Flow Rate | 250°C/5.0 kg | ISO 1133 | 16 | g/10 min |
| Melt Volume flow Rate | 250°C/5.0 kg | ISO 1133 | 15.0 | cm3/10min |
| Specific Volume | ASTM D792 | 0.830 | cm³/g | |
| Outdoor Suitability | UL 746C | f2 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- 7, 8 | ISO 178 | 80.0 | Mpa |
| Yield, 50.0 mm Span 6 | ASTM D790 | 84.0 | Mpa | |
| Tensile Modulus | -- 3 | ASTM D638 | 2250 | Mpa |
| -- 4 | ASTM D638 | 2250 | Mpa | |
| -- | ISO 527-2/1 | 2050 | Mpa | |
| Tensile Elongation | Yield 5 | ASTM D638 | 4.0 | % |
| Yield | ISO 527-2/50 | 4.0 | % | |
| Break 5 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/50 | 120 | % | |
| Flexural Modulus | 50.0 mm Span 6 | ASTM D790 | 2030 | Mpa |
| -- 7 | ISO 178 | 2000 | Mpa | |
| Tensile Strength | Yield 5 | ASTM D638 | 53.0 | Mpa |
| Yield | ISO 527-2/50 | 50.0 | Mpa | |
| Break 5 | ASTM D638 | 51.0 | Mpa | |
| Break | ISO 527-2/50 | 50.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D152511 | 122 | °C |
| -- | ISO 306/B50 | 120 | °C | |
| -- | ISO 306/B120 | 125 | °C | |
| RTI | UL 746 | 75.0 | °C | |
| RTI Imp | UL 746 | 75.0 | °C | |
| RTI Elec | UL 746 | 75.0 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 40°C | ASTM E831, ISO 11359-2 | 9.5E-5 | cm/cm/°C |
| Across Flow : -40 to 40°C | ASTM E831 | 9.0E-5 | cm/cm/°C | |
| Across Flow : -40°C | ISO 11359-2 | 9.0E-5 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 107 | °C |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 84.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 99.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | ISO 75-2/Af | 75.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 1 | ||
| Hot-wire Ignition | UL 746 | PLC 3 | ||
| High Voltage Arc Tracking Rate | UL 746 | PLC 0 | ||
| High Amp Arc Ignition | UL 746 | PLC 0 | ||
| Arc Resistance | ASTM D495 | PLC 5 |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature | 110 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 260 到 275 | °C | ||
| Mold Temperature | 65 到 90 | °C | ||
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 50 到 80 | % | ||
| Rear Temperature | 245 到 265 | °C | ||
| Middle Temperature | 250 到 270 | °C | ||
| Front Temperature | 255 到 275 | °C | ||
| Nozzle Temperature | 255 到 270 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 50 到 80 | rpm | ||
| Vent Depth | 0.013 到 0.020 | mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 60.0 | J |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame Rating | 1.5 mm | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.