PC/PBT XENOY™ 5720U-GY4F041 SABIC INNOVATIVE US
91
- Unit Price:
- $3621 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Chemical resistance Low temperature impact re
- Application Areas:Electronic display Household daily necessiti Lighting applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | Saturation, 23°C | ISO 62 | 0.28 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.080 | % | |
| Specific Volume | ASTM D792 | 0.850 | cm³/g | |
| Melt Mass-Flow Rate | 250°C/2.16 kg | ASTM D1238 | 3.8 | g/10 min |
| 250°C/5.0 kg | ASTM D1238, ISO 1133 | 11 | g/10 min | |
| 265°C/2.16 kg | ASTM D1238 | 6.0 | g/10 min | |
| 266°C/5.0 kg | ASTM D1238 | 20 | g/10 min | |
| 250°C/2.16 kg | ISO 1133 | 3.0 | g/10 min | |
| Melt Volume flow Rate | 250°C/2.16 kg | ISO 1133 | 3.00 | cm3/10min |
| 250°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min | |
| 265°C/2.16 kg | ISO 1133 | 6.00 | cm3/10min | |
| 265°C/5.0 kg | ISO 1133 | 18.0 | cm3/10min | |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 1.0 到 1.2 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Stress | -- 9, 10 | ISO 178 | 71.0 | Mpa |
| Yield, 50.0 mm Span 8 | ASTM D790 | 70.0 | Mpa | |
| Break, 50.0 mm Span 8 | ASTM D790 | 69.0 | Mpa | |
| Tensile Modulus | -- 2 | ASTM D638 | 1830 | Mpa |
| -- 3 | 内部方法 | 1830 | Mpa | |
| -- 4 | ASTM D638 | 1810 | Mpa | |
| -- | ISO 527-2/1 | 1790 | Mpa | |
| Tensile Elongation | Yield 7 | ASTM D638 | 4.6 | % |
| Yield 6 | 内部方法 | 4.6 | % | |
| Yield 5 | ASTM D638 | 4.0 | % | |
| Yield | ISO 527-2/5 | 4.1 | % | |
| Yield | ISO 527-2/50 | 4.6 | % | |
| Break 7 | ASTM D638 | 120 | % | |
| Break 6 | 内部方法 | 110 | % | |
| Break 5 | ASTM D638 | 120 | % | |
| Break | ISO 527-2/5 | 110 | % | |
| Break | ISO 527-2/50 | 120 | % | |
| Flexural Modulus | 50.0 mm Span 8 | ASTM D790 | 1660 | Mpa |
| -- 9 | ISO 178 | 1860 | Mpa | |
| Tensile Strength | Yield 5 | ASTM D638 | 47.0 | Mpa |
| Yield 6 | 内部方法 | 45.0 | Mpa | |
| Yield 7 | ASTM D638 | 44.0 | Mpa | |
| Yield | ISO 527-2/5 | 44.0 | Mpa | |
| Yield | ISO 527-2/50 | 47.0 | Mpa | |
| Break 7 | ASTM D638 | 50.0 | Mpa | |
| Break 6 | 内部方法 | 47.0 | Mpa | |
| Break 5 | ASTM D638 | 48.0 | Mpa | |
| Break | ISO 527-2/5, ISO 527-2/50 | 43.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ASTM D152513, ISO 306/B5013 | 119 | °C |
| -- | ISO 306/B120 | 122 | °C | |
| Linear thermal expansion coefficient | Flow : -40 to 95°C | ASTM E831 | 9.8E-5 | cm/cm/°C |
| Flow : -30 to 80°C | ISO 11359-2 | 9.8E-5 | cm/cm/°C | |
| Across Flow : -40 to 95°C | ASTM E831 | 1.0E-4 | cm/cm/°C | |
| Across Flow : -30 to 80°C | ISO 11359-2 | 1.0E-4 | cm/cm/°C | |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 3.20 mm | ASTM D648 | 108 | °C |
| 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 117 | °C | |
| 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12 | ISO 75-2/Bf | 109 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | ASTM D648 | 83.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 95.0 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 12 | ISO 75-2/Af | 87.0 | °C |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 4.0 到 6.0 | hr | ||
| Suggested Shot Size | 50 到 80 | % | ||
| Rear Temperature | 245 到 265 | °C | ||
| Middle Temperature | 250 到 270 | °C | ||
| Front Temperature | 255 到 275 | °C | ||
| Nozzle Temperature | 255 到 270 | °C | ||
| Back Pressure | 0.300 到 0.700 | Mpa | ||
| Screw Speed | 50 到 80 | rpm | ||
| Vent Depth | 0.013 到 0.020 | mm | ||
| Drying Temperature | 110 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 260 到 275 | °C | ||
| Mold Temperature | 65 到 90 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 47 | kJ/m² |
| 23°C | ISO 179/1eA | 55 | kJ/m² | |
| Instrumented Dart Impact | -40°C, Energy at Peak | ASTM D3763 | 49.0 | J |
| -40°C, Total Energy | ASTM D3763 | 59.0 | J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 | J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 | J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 | J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 | J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 | J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.