PC/PBT XENOY™ HX6600HP 8H4D023 SABIC INNOVATIVE US
32
- Unit Price:
- $3041 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 29MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 1.2to1.6 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.40 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.050 | % | |
| Melt Mass-Flow Rate | 250°C/5.0kg | ASTMD1238 | 11 | g/10min |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 10.0 | cm3/10min |
| Melt Viscosity | 260°C,1500sec^-1 | ISO11443 | 210 | Pa·s |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Modulus | ISO527-2/1 | 1900 | Mpa | |
| Tensile Stress | Yield | ISO527-2/50 | 44.0 | Mpa |
| Break | ISO527-2/50 | 37.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/50 | 4.0 | % |
| Break | ISO527-2/50 | 100 | % | |
| Tensile Elongation | Yield | ASTMD638 | 4.0 | % |
| Tensile Modulus | ASTMD638 | 1900 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 35.0 | Mpa |
| Yield | ASTMD638 | 43.0 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 1900 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 43.0 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 150 | % |
| Flexural Modulus | ISO178 | 1800 | Mpa | |
| Flexural Strength | ISO178 | 64.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 95.0 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 60.0 | °C | |
| Linear thermal expansion coefficient | TD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| MD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| MD：-40to40°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| MD：23to60°C | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1E-04 | cm/cm/°C | |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 60.0 | °C |
| Vicat Softening Temperature | ASTMD152510 | 117 | °C | |
| -- | ISO306/B50 | 117 | °C | |
| -- | ISO306/B120 | 120 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 100 | J | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 100 | J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 70 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 20 | kJ/m² |
| 23°C | ISO180/1A | 65 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| UnnotchedIzodImpactStrength8 | -40°C | ISO180/1U | NoBreak |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.