| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | 内部方法 | 0.80到1.1 | % |
| Modeling Shrinkage | TD | 内部方法 | 0.80到1.1 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.50 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.15 | % |
| Melt Volume flow Rate | 250°C/2.16kg | ISO1133 | 9.00 | cm3/10min |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 27.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 74.0 | Mpa |
| Tensile Stress | Yield | ISO527-2/50 | 54.0 | Mpa |
| Tensile Stress | Break | ISO527-2/50 | 42.0 | Mpa |
| Tensile Strain | Yield | ISO527-2/50 | 5.0 | % |
| Tensile Strain | Break | ISO527-2/50 | 100 | % |
| Tensile Modulus | | ISO527-2/1 | 2100 | Mpa |
| Flexural Modulus | | ISO178 | 2000 | Mpa |
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 30.0 | mg |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 0.45MPa, Unannealed,100mm Span | | ISO75-2/Be | 110 | °C |
| 1.8MPa, Unannealed,100mm Span | | ISO75-2/Ae | 80.0 | °C |
| Linear thermal expansion coefficient | MD:23to80°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD:23to80°C | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Thermal Conductivity | | ISO8302 | 0.18 | W/m/K |
| Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
| -- | | ISO306/A50 | 190 | °C |
| -- | | ISO306/B50 | 125 | °C |
| -- | | ISO306/B120 | 128 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+14 | ohms·cm |
| Dielectric Strength | 0.800mm,in Oil | IEC60243-1 | 32 | KV/mm |
| Dielectric Strength | 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm |
| Dielectric Strength | 3.20mm,in Oil | IEC60243-1 | 17 | KV/mm |
| Dissipation Factor? | 50Hz | IEC60250 | 2E-03 | |
| Dissipation Factor? | 60Hz | IEC60250 | 2E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 0.020 | |
| Relative Permittivity | 50Hz | IEC60250 | 2.80 | |
| Relative Permittivity | 60Hz | IEC60250 | 2.80 | |
| Relative Permittivity | 1MHz | IEC60250 | 2.90 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 无断裂 | |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 18 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 45 | kJ/m² |
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | 无断裂 | |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 20 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 50 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 100 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.50mm | UL94 | HB | |
| UL flame retardant rating | 3.00mm | UL94 | HB | |
| Glow Wire Flammability Index | 3.20mm | IEC60695-2-12 | 750 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.