PC/PBT XENOY™ X2500UV-BK1D355BZDD SABIC INNOVATIVE US

108

Unit Price:
$3252 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
23MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:High impact No fill
Application Areas:Electronic and electrical Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD3	内部方法	0.50到0.80	%
	Modeling Shrinkage	MD:3.20mm	内部方法	0.50到0.80	%
		Modeling Shrinkage	TD3	内部方法	0.50到0.80	%
			Modeling Shrinkage	MD2	内部方法	0.50到0.80	%
			Modeling Shrinkage	Modeling Shrinkage	TD2	内部方法	0.50到0.80	%
Moisture Absorption	Saturation,23°C	ISO62	0.70	%
Moisture Absorption	Moisture Absorption	Equilibrium,23°C,50%RH	ISO62	0.20	%
Melt Mass-Flow Rate	265°C/2.16kg	ASTMD1238	9.0	g/10min
Melt Volume flow Rate	265°C/1.2kg	ISO1133	4.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Taber Abrasion Resistance	1000Cycles,1000g,CS-17Wheel	内部方法	20.0	mg
Tensile Strength	Yield4	ASTMD638	56.0	Mpa
	Tensile Strength	Break4	ASTMD638	55.0	Mpa
		Tensile Strength	Break5	ASTMD638	55.0	Mpa
			Tensile Strength	Break	ISO527-2/50	56.0	Mpa
				Tensile Strength	Yield	ASTMD638	53.0	Mpa
					Tensile Strength	Yield5	ASTMD638	56.0	Mpa
					Tensile Strength	Tensile Strength	Yield	ISO527-2/50	57.0	Mpa
Tensile Modulus	--4	ASTMD638	2200	Mpa
	Tensile Modulus	--	ISO527-2/1	2200	Mpa
	Tensile Modulus	Tensile Modulus	--3	ASTMD638	2200	Mpa
Tensile Elongation	Yield4	ASTMD638	5.0	%
	Tensile Elongation	Break4	ASTMD638	80	%
		Tensile Elongation	Yield	ASTMD638,ISO527-2/50	5.0	%
			Tensile Elongation	Yield5	ASTMD638	5.0	%
				Tensile Elongation	Break	ASTMD638	100	%
					Tensile Elongation	Break5	ASTMD638	80	%
					Tensile Elongation	Tensile Elongation	Break	ISO527-2/50	70	%
Flexural Modulus	--	ASTMD790	2100	Mpa
	Flexural Modulus	50.0mmSpan6	ASTMD790	2150	Mpa
		Flexural Modulus	--7	ISO178	2150	Mpa
			Flexural Modulus	50.0mmSpan5	ASTMD790	2150	Mpa
			Flexural Modulus	Flexural Modulus	--6	ISO178	2150	Mpa
Flexural Strength	--6,7	ISO178	80.0	Mpa
	Flexural Strength	Yield,50.0mmSpan5	ASTMD790	79.0	Mpa
		Flexural Strength	--	ASTMD790	79.0	Mpa
			Flexural Strength	--7,8	ISO178	80.0	Mpa
			Flexural Strength	Flexural Strength	Yield,50.0mmSpan6	ASTMD790	79.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	1.8MPa,Unannealed,64.0mmSpan10	ISO75-2/Af	108	°C
	Deflection Temperature Under Load?	0.45MPa,Unannealed,64.0mmSpan11	ISO75-2/Bf	126	°C
		Deflection Temperature Under Load?	1.8MPa,Unannealed,3.20mm	ASTMD648	108	°C
			Deflection Temperature Under Load?	1.8MPa,Unannealed,64.0mmSpan11	ISO75-2/Af	108	°C
			Deflection Temperature Under Load?	Deflection Temperature Under Load?	0.45MPa,Unannealed,64.0mmSpan10	ISO75-2/Bf	126	°C
Vicat Softening Temperature	--	ASTMD152512,ISO306/B5012	135	°C
	Vicat Softening Temperature	--	ISO306/A50	145	°C
		Vicat Softening Temperature	--	ISO306/B120	136	°C
		Vicat Softening Temperature	Vicat Softening Temperature	--	ASTMD152511,ISO306/B5011	135	°C
Linear thermal expansion coefficient	MD:-40to40°C	ASTME831	8E-05	cm/cm/°C
	Linear thermal expansion coefficient	MD:23to80°C	ISO11359-2	8.2E-05	cm/cm/°C
		Linear thermal expansion coefficient	TD:-40to40°C	ASTME831	8.5E-05	cm/cm/°C
		Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD:23to80°C	ISO11359-2	8.7E-05	cm/cm/°C
Thermal Conductivity		ISO8302	0.18	W/m/K
Ball PressureTest	125°C	IEC60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	3.20mm,in Oil	IEC60243-1	17	KV/mm
Relative Permittivity	50Hz	IEC60250	3.30
	Relative Permittivity	60Hz	IEC60250	3.30
	Relative Permittivity	Relative Permittivity	1MHz	IEC60250	3.10
Dissipation Factor?	50Hz	IEC60250	2E-03
	Dissipation Factor?	60Hz	IEC60250	2E-03
	Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.020
Surface Resistivity		IEC60093	>1.0E+15	ohms
Volume Resistivity		IEC60093	>1.0E+14	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Instrumented Dart Impact	23°C,TotalEnergy	ASTMD3763	60.0	J
Charpy Notched Impact Strength	-30°C	ISO179/1eA	30	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	50	kJ/m²
Charpy Notched Impact Strength	-30°C	ISO179/1eA	30	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179/1eA	50	kJ/m²
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	无断裂
Unnotched Izod Impact Strength	-30°C	ISO180/1U	无断裂
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	无断裂
Unnotched Izod Impact Strength	-30°C	ISO180/1U	无断裂

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness	H358/30	ISO2039-1	95.0	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm,TestingbySABIC	UL94	HB
Glow Wire Flammability Index	2.7mm	IEC60695-2-12	750	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.