PC/PBT XENOY™ X4830 SABIC INNOVATIVE US
35
- Unit Price:
- $4412 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.70to0.90 | % |
| Moisture Absorption | Saturation,23°C | ISO62 | 0.42 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.14 | % | |
| Melt Mass-Flow Rate | 266°C/5.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 6.00 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Taber Abrasion Resistance | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 30.0 | mg |
| Tensile Modulus | ASTMD638 | 3400 | Mpa | |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 3100 | Mpa |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 96.0 | Mpa |
| Flexural Strength | ISO178 | 90.0 | Mpa | |
| Flexural Modulus | ISO178 | 2900 | Mpa | |
| Tensile Stress | Yield | ISO527-2/5 | 55.0 | Mpa |
| Yield | ISO527-2/50 | 61.0 | Mpa | |
| Break | ISO527-2/5 | 60.0 | Mpa | |
| Break | ISO527-2/50 | 55.0 | Mpa | |
| Tensile Strain | Yield | ISO527-2/5 | 4.1 | % |
| Break | ISO527-2/5 | 120 | % | |
| Break | ISO527-2/50 | 110 | % | |
| Yield | ISO527-2/50 | 4.2 | % | |
| Tensile Modulus | ISO527-2/1 | 3200 | Mpa | |
| Tensile Elongation | Break3 | ASTMD638 | 150 | % |
| Break4 | ASTMD638 | 140 | % | |
| Yield | ASTMD638 | 4.5 | % | |
| Yield | ASTMD638 | 4.1 | % | |
| Tensile Strength | Yield | ASTMD638 | 60.0 | Mpa |
| Yield | ASTMD638 | 56.0 | Mpa | |
| Break3 | ASTMD638 | 60.0 | Mpa | |
| Break4 | ASTMD638 | 60.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTMD152511 | 133 | °C | |
| -- | ISO306/B50 | 133 | °C | |
| -- | ISO306/B120 | 135 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 125 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 106 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 6E-05 | cm/cm/°C |
| MD：-30to80°C | ISO11359-2 | 7.2E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 8.2E-05 | cm/cm/°C | |
| TD：-30to80°C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 97.0 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 119 | °C | |
| Thermal Conductivity | ISO8302 | 0.20 | W/m/K |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 110 | J | |
| Instrumented Dart Impact | -20°C,TotalEnergy | ASTMD3763 | 70.0 | J |
| 23°C,TotalEnergy | ASTMD3763 | 70.0 | J | |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 12 | kJ/m² |
| 23°C | ISO179/1eA | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Unnotched Izod Impact Strength | -30°C | ISO180/1U | NoBreak | |
| 23°C | ISO180/1U | NoBreak | ||
| Notched Izod Impact Strength | -30°C | ISO180/1A | 9.0 | kJ/m² |
| 0°C | ISO180/1A | 15 | kJ/m² | |
| 23°C | ISO180/1A | 45 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball Indentation Hardness | H358/30 | ISO2039-1 | 105 | Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.