Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：BlowMolded | 内部方法 | 1.2to1.6 | % |
| Modeling Shrinkage | MD：Injection | ASTMD955 | 0.50to0.70 | % |
| Density / Specific Gravity | | ASTMD792 | 1.17 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | 23°C | ASTMD638 | 1590 | Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 1620 | Mpa |
| Tensile Elongation | Yield,23°C2 | 内部方法 | 7.0 | % |
| Tensile Elongation | Yield,23°C3 | 内部方法 | 6.5 | % |
| Tensile Elongation | Yield,23°C | ASTMD638 | 7.0 | % |
| Tensile Elongation | Break,23°C | ASTMD638 | 140 | % |
| Flexural Modulus | 23°C | ASTMD790 | 1590 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 1530 | Mpa |
| Flexural Strength | Yield,23°C | ASTMD790 | 66.0 | Mpa |
| Tensile Stress | Yield,23°C2 | 内部方法 | 44.0 | Mpa |
| Tensile Stress | Yield,23°C3 | 内部方法 | 45.0 | Mpa |
| Tensile Stress | Yield,23°C | ISO527-2 | 45.0 | Mpa |
| Tensile Stress | Break,23°C | ISO527-2 | 49.0 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 130 | % |
| Tensile Strain | Yield,23°C | ISO527-2 | 7.0 | % |
| Tensile Strength | Break,23°C | ASTMD638 | 53.0 | Mpa |
| Tensile Strength | Yield,23°C | ASTMD638 | 44.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 109 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 92.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | -40°C | ASTMD256 | 130 | J/m |
| Notched Izod Impact Strength | 23°C | ASTMD256 | 650 | J/m |
| Notched Izod Impact Strength | 23°C3 | 内部方法 | 640 | J/m |
| Notched Izod Impact Strength | 23°C2 | 内部方法 | 650 | J/m |
| Notched Izod Impact Strength | -40°C | ISO180 | 14 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180 | 66 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ASTMD4812 | NoBreak | |
| Notched Izod Impact Strength | 23°C | ASTMD4812 | NoBreak | |
| Instrumented Dart Impact | -40°C,EnergyatMaxLoad | ASTMD3763 | 63.0 | J |
| Instrumented Dart Impact | 23°C,EnergyatMaxLoad | ASTMD3763 | 59.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Sale,23°C | ASTMD785 | 115 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | --2 | 内部方法 | <1.0 | % |
| Haze | -- | ASTMD1003 | <1.0 | % |
| Transmittance | Total | ASTMD1003 | 92.0 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| FillVolumeShrinkage4 | Boiling,1hr | 内部方法 | <1.0 | % |
| FillVolumeShrinkage4 | Boiling,2hr | 内部方法 | <1.5 | % |
| FillVolumeShrinkage4 | Dishwasher | 内部方法 | <1.0 | % |
| MicrowaveBoiling-OvenPower4 | | 内部方法 | <2200 | Watts |
| ThermalShock-WaterImmersion4 | 35to98°C | 内部方法 | Noeffect | |
| MicrowaveSteamSterilization-TotalEnergy4 | | 内部方法 | <11200 | W-min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.