Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23°C,24hr,0.250mm | ASTMD570 | 0.50 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Change in Haze | 23°C | ASTMD1044 | 23haze | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | MD:23°C,0.250mm | ASTMD696 | 9E-05 | cm/cm/°C |
Melting temperature | | | 110 | °C |
Specific Heat | 60°C | DSC | 1700 | J/kg/°C |
Specific Heat | 100°C | DSC | 1900 | J/kg/°C |
Specific Heat | 150°C | DSC | 2200 | J/kg/°C |
Specific Heat | 200°C | DSC | 2400 | J/kg/°C |
Specific Heat | 250°C | DSC | 2600 | J/kg/°C |
Film | Test Condition | Test Method | Test Result | Unit |
---|
Film Puncture Energy | 250µm | ASTMD3763 | 4.60 | J |
Film Thickness - Tested) | | | 250 | µm |
Oxygen Transmission Rate | 23°C,250µm,50%RH | ASTMD3985 | 32 | cm³·mm/m²/atm/24hr |
Water Vapor Transmission Rate | 23°C,100%RH,250µm | ASTMF1249 | 4.0 | g/m²/24hr |
Water Vapor Transmission Rate | 38°C,100%RH,250µm | ASTMF1249 | 11 | g/m²/24hr |
Secant Modulus | MD:250µm | ASTMD882 | 1500 | Mpa |
Secant Modulus | TD:250µm | ASTMD882 | 1400 | Mpa |
Tensile Elongation | MD:Yield,250μm | ASTMD882 | 7.0 | % |
Tensile Elongation | TD:Yield,250μm | ASTMD882 | 7.0 | % |
Tensile Elongation | MD:Break,250μm | ASTMD882 | 180 | % |
Tensile Elongation | TD:Break | ASTMD882 | 200 | % |
Tensile Strength | TD:Yield,250μm | ASTMD882 | 40.0 | Mpa |
Tensile Strength | MD:Break,250μm | ASTMD882 | 59.0 | Mpa |
Tensile Strength | TD:Break,250μm | ASTMD882 | 52.0 | Mpa |
Tensile Strength | MD:Yield,250μm | ASTMD882 | 41.0 | Mpa |
Tearing Strength | TD:250µm | ISO6383-1 | 11.0 | N/mm |
Tearing Strength | MD:250µm | ISO6383-1 | 11.0 | N/mm |
CarbonDioxidePermeability6 | 23°C,254.0µm | ASTMD1434 | 150 | cm³·mm/m²/atm/24hr |
ElmendorfTearStrength | MD:23°C,250.0µm | ASTMD1922 | 5 | N |
ElmendorfTearStrength | TD:23°C,250.0µm | | 6 | N |
PPTTearResistance | MD:23°C,250.0µm | - | 42 | N |
PPTTearResistance | TD:23°C,250.0µm | - | 56 | N |
Tearing Strength | MD:23°C,250.0µm | ASTMD1938 | 410 | gf |
Tearing Strength | TD:23°C,250.0µm | ASTMD1938 | 310 | gf |
Gardner Impact | -30°C,250µm | ASTMD1709A | 910 | g |
Gardner Impact | 23°C,250µm | ASTMD1709A | 880 | g |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
The Yellow Index | 250mm | ASTMD1925 | 0.50 | YI |
UVTransmittance10 | 250.0µm | | 89 | % |
Refractive index of light | | ASTMD542 | 1.550 | |
Gloss | 60°,250µm | ASTMD2457 | 161 | |
Transmittance | 250µm | ASTMD1003 | 92.0 | % |
Haze | 250µm | ASTMD1003 | 0.70 | % |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
SurfaceEnergy | Dispersive:23°C,250.0µm | ASTMD5946 | 39 | dyne/cm |
SurfaceEnergy | Polar:23°C,250mm | ASTMD5946 | 8 | dyne/cm |
SurfaceEnergy | Total:23°C,250.0µm | ASTMD5946 | 46 | dyne/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.