Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23°C,24hr,0.254mm | ASTMD570 | 0.50 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| TaberAbrasionResistance2 | 23°C,250.0µm | ASTMD1044 | 20Haze | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Specific Heat | 60°C | DSC | 1700 | J/kg/°C |
| Specific Heat | 100°C | DSC | 1900 | J/kg/°C |
| Specific Heat | 150°C | DSC | 2300 | J/kg/°C |
| Specific Heat | 200°C | DSC | 2400 | J/kg/°C |
| Specific Heat | 250°C | DSC | 2600 | J/kg/°C |
| Linear thermal expansion coefficient | MD：23°C | ASTMD696 | 8E-05 | cm/cm/°C |
| Melting temperature | | | 119 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength-MD | Yield,250μm | ASTMD882 | 43.0 | Mpa |
| Elongation - MD | Break,250μm | ASTMD882 | 110 | % |
| Tearing Strength | MD:23°C,250.0µm | ASTMD1938 | 310 | gf |
| Tearing Strength | TD:23°C,250.0µm | ASTMD1938 | 200 | gf |
| Film Puncture Energy | 250µm | ASTMD3763 | 4.50 | J |
| Film Thickness - Tested) | | | 250 | µm |
| Tensile Strain (MD) | Yield,250µm | ASTMD882 | 8.0 | % |
| Secant Modulus (TD) | 250µm | ASTMD882 | 1500 | Mpa |
| Secant Modulus (TD) | 250µm | ASTMD882 | 1400 | Mpa |
| Tensile Strength (MD) | Break,250µm | ASTMD882 | 57.0 | Mpa |
| Tensile Strength (TD) | Break,250µm | ASTMD882 | 42.0 | Mpa |
| Tensile Strength (TD) | Yield,250µm | ASTMD882 | 41.0 | Mpa |
| Tensile Strain (TD) | Break,250µm | ASTMD882 | 120 | % |
| Tensile Strain (TD) | Yield,250µm | ASTMD882 | 8.0 | % |
| Oxygen Transmission Rate | 23°C,250µm,50%RH | ASTMD3985 | 44 | cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | 23°C,100%RH,250µm | ASTMF1249 | 4.0 | g/m²/24hr |
| Water Vapor Transmission Rate | 38°C,100%RH,250µm | ASTMF1249 | 10 | g/m²/24hr |
| Elmendorf Tear Strength | TD:23°C,250.0µm | ASTMD1922 | 4 | N |
| Elmendorf Tear Strength | MD:23°C,250.0µm | ASTMD1922 | 4 | N |
| Tearing Strength | MD:250µm | ISO6383-1 | 10.0 | N/mm |
| Tearing Strength | TD:250µm | ISO6383-1 | 9.00 | N/mm |
| PPTTearResistance | MD:23°C,250.0µm | - | 40 | N |
| PPTTearResistance | TD:23°C,250.0µm | - | 40 | N |
| Gardner Impact | -30°C,250µm | ASTMD1709A | 830 | g |
| Gardner Impact | -18°C,250µm | ASTMD1709A | 830 | g |
| Gardner Impact | 23°C,250µm | ASTMD1709A | 830 | g |
| CarbonDioxidePermeability | 23°C,254.0µm | ASTMD1434 | 210 | cm³·mm/m²/atm/24hr |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| The Yellow Index | 250mm | ASTMD1925 | 0.50 | YI |
| UVTransmittance8 | 250.0µm | | 89 | % |
| Transmittance | 250µm | ASTMD1003 | 93.0 | % |
| Refractive index of light | | ASTMD542 | 1.540 | |
| Gloss | 60°,250µm | ASTMD2457 | 158 | |
| Haze | 250µm | ASTMD1003 | 0.80 | % |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| SurfaceEnergy | Dispersive:23°C,250.0µm | ASTMD5946 | 39 | dyne/cm |
| SurfaceEnergy | Polar:23°C,250.0µm | ASTMD5946 | 8 | dyne/cm |
| SurfaceEnergy | Total:23°C,250.0µm | ASTMD5946 | 47 | dyne/cm |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.