Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.20mm | ASTMD955 | 0.20to0.50 | % |
Moisture Absorption | 23°C,24hr | ASTMD570 | 0.13 | % |
Moisture Absorption | 23°C,24hr | ISO62 | 0.13 | % |
Density / Specific Gravity | | ASTMD792 | 1.23 | g/cm³ |
Density / Specific Gravity | 23°C | ISO1183 | 1.23 | g/cm³ |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Strength | Break,23°C | ASTMD638 | 52.0 | Mpa |
Tensile Strength | Yield,23°C | ASTMD638 | 45.0 | Mpa |
Tensile Strain | Break,23°C,4.00mm | ISO527-2 | 230 | % |
Tensile Strain | Yield,23°C,4.00mm | ISO527-2 | 4.4 | % |
Tensile Strength | Yield,23°C,4.00mm | ISO527-2 | 46.0 | Mpa |
Tensile Strength | Break,23°C,4.00mm | ISO527-2 | 47.0 | Mpa |
Tensile Elongation | Yield,23°C | ASTMD638 | 5.0 | % |
Tensile Elongation | Break,23°C | ASTMD638 | 330 | % |
Flexural Modulus | 23°C | ASTMD790 | 1800 | Mpa |
Flexural Modulus | 23°C,4.00mm | ISO178 | 1800 | Mpa |
Flexural Strength | 23°C,4.00mm | ISO178 | 63.0 | Mpa |
Flexural Strength | Yield,23°C | ASTMD790 | 66.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 74.0 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 74.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 64.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 65.0 | °C |
Specific Heat | 60°C | DSC | 1340 | J/kg/°C |
Specific Heat | 240°C | DSC | 2050 | J/kg/°C |
Specific Heat | 导热系数(23°C) | DSC | 0.19 | W/m/K |
Vicat Softening Temperature | | ASTMD15252 | 88.0 | °C |
Vicat Softening Temperature | -- | ISO306/A | 88.0 | °C |
Vicat Softening Temperature | -- | ISO306/B | 79.0 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C | ISO180 | 130 | kJ/m² |
Notched Izod Impact Strength | -40°C | ASTMD4218 | NoBreak | |
Notched Izod Impact Strength | 23°C | ASTMD4218 | NoBreak | |
Notched Izod Impact Strength | -40°C | ASTMD256 | 64 | J/m |
Notched Izod Impact Strength | 23°C | ASTMD256 | NoBreak | |
Notched Izod Impact Strength | -40°C | ISO180 | 7.4 | kJ/m² |
Multi-Axial Instrumented Impact Energy | -40°C,能量to力量峰值 | ISO6603-2 | 16.0 | J |
Multi-Axial Instrumented Impact Energy | 23°C,能量to力量峰值 | ISO6603-2 | 14.0 | J |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale,23°C | ASTMD785 | 105 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.6mm | UL94 | HB | |
UL flame retardant rating | 3.2mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.