Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.30 | % |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.15 | % |
| Melt flow rate | 300°C/1.2 kg | ASTM D1238 | 20 | g/10 min |
| General transmittance | | D1003 | 89% | |
| Total transmittance | | D1003 | 91% | |
| Light Mist | | D1003 | 0.3% | |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | @Yield | D638 | 47MPa（6900 psi） | |
| Tensile stress | @Break | D638 | 51MPa（7400 psi） | |
| Stretching degree | @Yield | D638 | 5% | |
| Stretching degree | @Break | D638 | 320% | |
| Stretching degree | @Yield | ISO 527 | 4% | |
| Stretching degree | @Break | ISO 527 | 200% | |
| Flexural strength | | ISO 178 | 65MPa | |
| Impact resistance (perforation), energy @ maximum load | @23℃(73℉) | D3763 | 42 J(31 ft bf) | |
| Impact resistance (perforation), energy @ maximum load | @-40℃(-40℉) | D3763 | 48 J/m(35 ft bf) | |
| Suspended beam impact strength | @23℃，切口 | ISO 180 | 7.8kJ/m | |
| Suspended beam impact strength | @-40℃，切口 | ISO 180 | 4.8kJ/m | |
| Suspended beam impact strength | @23℃(73?H)，切口 | D256 | 80 J/m(1.5 ft bf/in) | |
| Suspended beam impact strength | @-40℃(-40?H)，切口 | D256 | 40 J/m(0.7 ft bf/in) | |
| Flexural modulus | | D790 | 2000MPa(2.9×10 | |
| Flexural modulus | | ISO 178 | 1850MPa | |
| Tensile modulus | | ISO 527 | 1800MPa | |
| elongation | Break | ASTM D638 | 15 | % |
| Rockwell hardness | R刻度 | D785 | 103 | |
| Tensile strength | Yield | ASTM D638 | 60.0 | Mpa |
| Tensile strength | @Yield | ISO 527 | 47MPa | |
| Tensile strength | @Break | ISO 527 | 46MPa | |
| impact strength | @23℃(73℉)，未切口 | D4812 | NB J/m(NB ft bf/in) | |
| impact strength | @-40℃(-40℉)，未切口 | D4812 | NB J/m(NB ft bf/in) | |
| Flexural yield strength | | D790 | 69MPa(10000 psi) | |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Bending temperature | 0.455MPa(66 psi) | D648 | 73℃(164℉) | |
| Bending temperature | 1.82MPa(264 psi) | D648 | 65℃(149℉) | |
| Thermal deformation temperature under load | 0.45 MPa, Unannealed | ASTM D648 | 135 | °C |
| Thermal deformation temperature under load | 1.8 MPa, Unannealed | ASTM D648 | 125 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | 2.00 mm | ASTM D149 | 15 | KV/mm |
| Volume resistivity | | ASTM D257 | > 1.0E+16 | ohms·cm |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| drying temperature | | | 70℃(160℉) | |
| drying time | | | 6小时 | |
| Plastic film temperature | | | 15-30℃(60-80℉) | |
| Processing melting temperature | | | 230-280℃(450-530℉) | |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| drying time | | | 3.0 到 4.0 | hr |
| Temperature at the rear of the barrel | | | 265 到 275 | °C |
| Temperature in the middle of the barrel | | | 280 到 290 | °C |
| Spray nozzle temperature | | | 285 到 295 | °C |
| drying temperature | | | 120 | °C |
| Processing (melt) temperature | | | 280 到 290 | °C |
| Mold temperature | | | 60 到 80 | °C |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 3.2 mm | UL 94 | V-2 | |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | D792 | 1.2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.