Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:23°C | ISO294-4 | 0.60到0.80 | % |
Modeling Shrinkage | MD,23℃ | ISO 294-4 | 0.60 到 0.80 | % |
Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 90.0 | cm3/10min |
Melt Volume flow Rate | 220℃/2.16 kg | ISO 1133 | 90.0 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Modulus | 23°C | ISO178 | 2550 | Mpa |
Flexural Stress | 23°C | ISO178 | 68.0 | Mpa |
Charpy Notched Impact Strength | -30℃ | ISO 179 | 2.0 | kJ/m² |
Tensile Stress | 23℃ | ISO 527-2 | 43.0 | Mpa |
Tensile Stress | 23°C | ISO527-2 | 43.0 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 2280 | Mpa |
Tensile Modulus | 23℃ | ISO 527-2 | 2280 | Mpa |
Rockwell Hardness | 23℃ | ISO 2039-2 | 104 | R 计秤 |
Flexural Modulus | 23℃ | ISO 178 | 2550 | Mpa |
Flexural Strength | 23℃ | ISO 178 | 68.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.80MPa,Unannealed | ISO 75-2/Af | 72.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 72.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 8E-05 | cm/cm/°C |
Flame Rating | 0.800mm | UL 94 | V-2 | |
Coefficient of Linear Thermal Expansion | Flow | ISO 11359-2 | 0.000080 | cm/cm/℃ |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Sale,23°C | ISO2039-2 | 104 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.8mm | UL94 | V-2 | |
UL flame retardant rating | 3.0mm | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.