Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 0.10 | % |
| Melt Volume flow Rate | 230°C/2.16 kg | ISO 1133 | 15.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | ISO 527-2 | 36.0 | Mpa |
| Tensile Stress | 5.0% Strain | ISO 527-2 | 15.0 | Mpa |
| Tensile Stress | 10% Strain | ISO 527-2 | 20.0 | Mpa |
| Tensile Stress | 50% Strain | ISO 527-2 | 23.0 | Mpa |
| Tensile Stress | 100% Strain | ISO 527-2 | 20.0 | Mpa |
| Nominal Tensile Strain at Break | | ISO 527-2 | 460 | % |
| Tensile Modulus | | ISO 527-2 | 330 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO 306/B50 | 95.0 | °C |
| Melting Temperature | | ISO 11357-3 | 205 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | > 1.0E+15 | ohms·cm |
| Dissipation Factor? | 1 MHz | IEC 60250 | 0.050 | |
| Dielectric Strength | | IEC 60243-1 | 14 | KV/mm |
| Relative Permittivity | 100 Hz | IEC 60250 | 4.30 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore A, 3 sec | ISO 868 | 98 | |
| Shore Hardness | Shore A, 15 sec | ISO 868 | 98 | |
| Shore Hardness | Shore D, 3 sec | ISO 868 | 64 | |
| Shore Hardness | Shore D, 15 sec | ISO 868 | 61 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flammability level | 0.75 mm | IEC 60695-11-10, -20 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.