Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24 hr, 23°C | ASTM D570 | 0.60 | % |
Melt Mass-Flow Rate | 230°C/2.16 kg | ASTM D1238 | 42 | g/10 min |
Modeling Shrinkage - Flow | | ASTM D955 | 1.1 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Break, 3.20 mm | ASTM D638 | 910 | % |
Flexural Modulus | 3.20 mm | ASTM D790 | 83.0 | Mpa |
Flexural Strength | 3.20 mm | ASTM D790 | 6.00 | Mpa |
Tensile Strength | Break, 3.20 mm | ASTM D638 | 23.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTM D15253 | 165 | °C |
Peak Melting Temperature | | ASTM D3418 | 184 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Time | | | 3.0 到 8.0 | hr |
Rear Temperature | | | 180 到 190 | °C |
Middle Temperature | | | 200 到 220 | °C |
Front Temperature | | | 210 到 220 | °C |
Nozzle Temperature | | | 210 到 220 | °C |
Drying Temperature | | | 100 到 110 | °C |
Suggested Max Moisture | | | < 0.10 | % |
Mold Temperature | | | 20 到 40 | °C |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D | ASTM D2240 | 45 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.8 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.