TPEE DYM100 NC010 DUPONT BELGIUM
76
- Unit Price:
- $6593 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 15.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact Medium rigidity
- Application Areas:engineering application Automotive components
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.8 | % |
| MD | ISO294-4 | 2.2 | % | |
| Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.90 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
| MediumDensity | 1.19 | g/cm³ | ||
| SpecificHeatCapacityofMelt | 3000 | J/kg/°C | ||
| Melt Mass-Flow Rate | ISO1133 | 2.3 | g/10min | |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 1.90 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Creep Modulus | 1hr | ISO899-1 | 2900 | Mpa |
| Nominal Tensile Strain at Break | ISO527-2 | 45 | % | |
| Flexural Stress | 3.5%Strain | ISO178 | 79.0 | Mpa |
| Compressive Stress | ISO604 | 110 | Mpa | |
| Tensile Stress | Yield | ISO527-2 | 72.0 | Mpa |
| Tensile Strain | Yield | ISO527-2 | 26 | % |
| Tensile Creep Modulus | 1000hr | ISO899-1 | 1600 | Mpa |
| Tensile Modulus | ISO527-2 | 3000 | Mpa | |
| Flexural Modulus | ISO178 | 2900 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 160 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 100 | °C | |
| Vicat Softening Temperature | -- | ISO306/A50 | 175 | °C |
| -- | ISO306/B50 | 160 | °C | |
| Linear thermal expansion coefficient | MD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| TD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 1E-04 | cm/cm/°C | |
| TD：AnnealingTemperature | ISO11359-2 | 160 | °C | |
| TD：AnnealingTime-Optional | ISO11359-2 | 30.0 | min/mm | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1E-07 | m²/s | |
| MD：-- | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Melting Temperature | ISO11357-3 | 178 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC60093 | 3E+13 | ohms | |
| Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric Strength | IEC60243-1 | 41 | KV/mm | |
| Dissipation Factor? | 100Hz | IEC60250 | 1E-03 | |
| 1MHz | IEC60250 | 5.5E-03 | ||
| Relative Permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.80 | ||
| Comparative Tracking Index | IEC60112 | 600 | V |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 430 | kJ/m² |
| 23°C | ISO179/1eU | NoBreak |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | M-Sale | ISO2039-2 | 90 | |
| R-Sale | ISO2039-2 | 121 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.8mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| FMVSS Flammability | FMVSS302 | B | ||
| atomization | F-value(refraction) | ISO6452 | 91 | % |
| G-value(condensate) | ISO6452 | 1E-04 | g | |
| Burning Rate | 1.00mm | ISO3795 | 30 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Emission | VDA275 | <8.00 | mg/kg | |
| EmissionofOrganicCompounds | VDA277 | 4.00 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.