Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 240°C/10.0kg | ISO1133 | 10 | g/10min |
Melt Volume flow Rate | 240°C/10.0kg | ISO1133 | 10.0 | cm3/10min |
Modeling Shrinkage | TD | ISO294-4 | 2.1 | % |
Modeling Shrinkage | MD | ISO294-4 | 2.2 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | 10%Strain | ISO527-2 | 11.9 | Mpa |
Tensile Stress | 50%Strain | ISO527-2 | 19.0 | Mpa |
Tensile Strain | Break | ISO527-2 | >300 | % |
Nominal Tensile Strain at Break | | ISO527-2 | 380 | % |
Tensile Modulus | | ISO527-2 | 190 | Mpa |
Tensile Stress | Break | ISO527-2 | 35.0 | Mpa |
Tensile Stress | 5.0%Strain | ISO527-2 | 7.80 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Brittleness Temperature | | ISO974 | -54.0 | °C |
Melting Temperature | | ISO11357-3 | 211 | °C |
Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tearing Strength (Flow) | | ISO34-1 | 140 | kN/m |
Fill Analysis | Test Condition | Test Method | Test Result | Unit |
---|
Melt Density | | | 1.01 | g/cm³ |
SpecificHeatCapacityofMelt | | | 2150 | J/kg/°C |
ThermalConductivityofMelt | | | 0.16 | W/m/K |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 无断裂 | |
Tensile Impact Strength | 23°C | ISO8256/1 | 330 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Shore Hardness | Shore D | ISO868 | 58 | |
Shore Hardness | Shore D,15sec | ISO868 | 52 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | 1.00mm | ISO3795 | 42 | mm/min |
Supplementary information | Test Condition | Test Method | Test Result | Unit |
---|
Odor | | VDA270 | 3.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.