TPEE Hytrel® DYM350 BK DUPONT USA

Unit Price:
$5805 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
42MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Moisture Absorption	23°C,24hr	ISO62	0.60	%
	Moisture Absorption	Saturation,23°C,2.00mm	ISO62	0.60	%
	Moisture Absorption	Moisture Absorption	Equilibrium,23°C,2.00mm,50%RH	ISO62	0.20	%
Modeling Shrinkage	TD	ISO294-4	1.4	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.3	%
Melt Mass-Flow Rate	240°C/2.16kg	ISO1133	15	g/10min
Melt Volume flow Rate	240°C/2.16kg	ISO1133	14.0	cm3/10min
MediumDensity			1.00	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Nominal Tensile Strain at Break		ISO527-2	600	%
Tensile Modulus		ISO527-2	370	Mpa
Flexural Modulus		ISO178	430	Mpa
Tensile Stress	Yield	ISO527-2	15.0	Mpa
	Tensile Stress	Break	ISO527-2	35.0	Mpa
		Tensile Stress	5.0%Strain	ISO527-2	10.5	Mpa
			Tensile Stress	10%Strain	ISO527-2	13.0	Mpa
			Tensile Stress	Tensile Stress	50%Strain	ISO527-2	16.0	Mpa
Tensile Strain	Yield	ISO527-2	43	%
Tensile Strain	Tensile Strain	Break	ISO527-2	>300	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	50.0	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	40.0	°C
Brittleness Temperature		ISO974	-100	°C
Glass Transition Temperature		ISO11357-2	-55.0	°C
Melting Temperature		ISO11357-3	222	°C
Linear thermal expansion coefficient	MD	ISO11359-2	1.8E-04	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD	ISO11359-2	1.8E-04	cm/cm/°C
Effective Thermal Diffusivity			5.44E-08	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength		IEC60243-1	20	KV/mm
Dissipation Factor?	100Hz	IEC60250	7E-03
Dissipation Factor?	Dissipation Factor?	1MHz	IEC60250	0.023
Surface Resistivity		IEC60093	5E+14	ohms
Volume Resistivity		IEC60093	>1.0E+15	ohms·cm
Relative Permittivity	100Hz	IEC60250	4.60
Relative Permittivity	Relative Permittivity	1MHz	IEC60250	4.40

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Multi-Axial Instrumented Impact Energy	23°C	ISO6603-2	39.0	J
Multi-Axial Instrumented Impact Peak Force	23°C	ISO6603-2	3200	N

hardness	Test Condition	Test Method	Test Result	Unit
Shore Hardness	Shore D	ISO868	55
Shore Hardness	Shore Hardness	Shore D,15sec	ISO868	50

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO4589-2	22	%
FMVSS Flammability		FMVSS302	SE/B
Burning Rate	1.00mm	ISO3795	23	mm/min

Supplementary information	Test Condition	Test Method	Test Result	Unit
EmissionofOrganicCompounds		VDA277	2.70	µgC/g
Odor		VDA270	5.00

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.