TPEE RITEFLEX® 640 CELANESE USA

Unit Price:
$3977 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
31MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:UV resistance
Application Areas:High temperature hot plug Automotive components
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	1.0	%
Modeling Shrinkage	Modeling Shrinkage	MD	ISO294-4	1.2to1.4	%
Melt Mass-Flow Rate		ASTMD1238	8.0to12	g/10min
Melt Mass-Flow Rate	Melt Mass-Flow Rate	220°C/2.16kg	ISO1133	10	g/10min
Specific Volume		ASTMD792	0.882	cm³/g
viscosity		内部方法	351	Pa·s
Shear		内部方法	1000	1/°C

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
RossFlex		内部方法	>1.0E+6	cycles
Flexural Stress	3.5%Strain	ISO178	3.00	Mpa
Flexural Stress	Flexural Stress	23°C	ISO178	5.00	Mpa
Tab	1000Cycles,CS-18Wheel	ASTMD4060	90.0	mg
Tensile Strength	Break,23°C	ASTMD638	20.7	Mpa
Tensile Stress	Break	ISO527-2/1A/50	17.0	Mpa
	Tensile Stress	5.0%Strain	ISO527-2	3.00	Mpa
		Tensile Stress	10%Strain	ISO527-2	5.00	Mpa
		Tensile Stress	Tensile Stress	50%Strain	ISO527-2/1A/50	8.00	Mpa
Tensile Strain	Break	ISO527-2/1A/50	>300	%
Tensile Modulus		ISO527-2/1A/1	75.0	Mpa
Tensile Modulus	Tensile Modulus	23°C	ASTMD638	92.4	Mpa
Tensile Elongation	Break,23°C	ASTMD638	480	%
Flexural Modulus	-40°C	ISO178	115	Mpa
Flexural Modulus	Flexural Modulus	23°C	ISO178	70.0	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	56.0	°C
Vicat Softening Temperature		ASTMD1525	136	°C
Brittleness Temperature		ISO974	-78.0	°C
Linear thermal expansion coefficient	MD	ISO11359-2	2.2E-04	cm/cm/°C
Glass Transition Temperature		ASTMD3418	-65.0	°C
Melting Temperature		ISO11357-3	170	°C
Peak Melting Temperature		ASTMD3418	180	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation Factor?	1MHz	IEC60250	0.030
Dielectric Strength		IEC60243-1	13	KV/mm
Relative Permittivity	1MHz	IEC60250	4.70
Comparative Tracking Index		ASTMD3638	>600	V
Comparative Tracking Index	Comparative Tracking Index		IEC60112	>600	V
Dielectric Strength		ASTMD149	12	KV/mm
Surface Resistivity		IEC60093	3E+15	ohms
Volume Resistivity		ASTMD257	5E+12	ohms·cm
Volume Resistivity	Volume Resistivity		IEC60093	5E+12	ohms·cm

Elastomers Properties	Test Condition	Test Method	Test Result	Unit
Shore Hardness		ASTMD2632	59	%
TearStrength-Flow2		ISO34-1	84	kN/m

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO179/1eU	NoBreak
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO179/1eU	NoBreak
Notched Izod impact strength	-30°C	ISO180/1U	NoBreak
Notched Izod impact strength	Notched Izod impact strength	23°C	ISO180/1U	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Durometer		内部方法	40.0
Shore Hardness	Shore D	ASTMD2240	40
Shore Hardness	Shore Hardness	Shore D,15sec	ISO868	40

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

Supplementary information	Test Condition	Test Method	Test Result	Unit
Tearing Strength		Kg/m	110.3	kN/m
Temperature		内部方法	220	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.