Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：2.00mm | ASTMD955 | 1.3 | % |
| Moisture Absorption | Equilibrium,23°C,65%RH | ASTMD570 | 0.36 | % |
| Melt Mass-Flow Rate | 230°C/2.16kg | ASTMD1238 | 20 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Taber Abrasion Resistance | 1000Cycles | ASTMD1044 | 10.0 | mg |
| Tensile Strength | Yield | ASTMD638 | 38.0 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 500 | % |
| Flexural Modulus | | ASTMD790 | 289 | Mpa |
| Compressive Modulus | | ASTMD695 | 19.1 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 117 | °C |
| Vicat Softening Temperature | | ASTMD1525 | 190 | °C |
| Brittleness Temperature | | ASTMD746 | -65.0 | °C |
| Linear thermal expansion coefficient | MD | ASTMD696 | 1.4E-04 | cm/cm/°C |
| Melting temperature | | DSC | 212 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | ASTMD149 | 30 | KV/mm |
| Volume Resistivity | | ASTMD257 | 2E+14 | ohms·cm |
| Elastomers Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 50%Strain | ASTMD412 | 19.6 | Mpa |
| Compression Set | | ASTMD395 | 60 | % |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D | ASTMD2240 | 57 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.