PPA Omnix® HPPA 4050 NT000 SOLVAY SHANGHAI
92
- Unit Price:
- $7897 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 16MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage (Across Flow) | ISO 294 | 0.5 | % | |
| Modeling Shrinkage (Flow) | ISO 294 | 0.1 | % | |
| Moisture Absorption (23°C 24hr) | ISO 62 | 0.24 | % | |
| Moisture Absorption (23°C) | 内部测试方法 | 3.8 | % | |
| Modeling Shrinkage | 内部测试方法 | 1.3 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength (Yield) | ISO 527 | 245 | Mpa | |
| Tensile Modulus | ISO 527 | 17000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO 11357 | 260 | °C | |
| Flexural Modulus | ISO 178 | 15000 | Mpa | |
| Tensile Elongation (Break) | ISO 527 | 2.6 | % | |
| Flexural Strength | ISO 178 | 350 | Mpa | |
| Charpy Notched Impact Strength | ISO 179 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | 100 | kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| CTI | IEC 60112 | V |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.