Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 0.90 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.40 | % |
Biobased Carbon Content | | ISO 16620-2 | 21 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO 527-2 | 11700 | Mpa |
Flexural Modulus | | ISO 178 | 11300 | Mpa |
Flexural Stress | | ISO 178 | 210 | Mpa |
Tensile Stress | Break | ISO 527-2 | 134 | Mpa |
Tensile Strain | Break | ISO 527-2 | 1.7 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Linear thermal expansion coefficient | Flow | ISO 11359-2 | 2.0E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Flow : -40 to 23°C | ISO 11359-2 | 1.7E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Flow : 55 to 160°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow | ISO 11359-2 | 5.1E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow : -40 to 23°C | ISO 11359-2 | 4.3E-5 | cm/cm/°C |
Linear thermal expansion coefficient | Across Flow : 55 to 160°C | ISO 11359-2 | 8.4E-5 | cm/cm/°C |
Melting Temperature | | ISO 11357-3 | 314 | °C |
RTI | 0.40 mm | UL 746 | 125 | °C |
RTI | 3.0 mm | UL 746 | 130 | °C |
RTI Imp | 0.40 mm | UL 746 | 115 | °C |
RTI Imp | 3.0 mm | UL 746 | 120 | °C |
RTI Elec | 0.40 mm | UL 746 | 130 | °C |
RTI Elec | 3.0 mm | UL 746 | 130 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC 60243-1 | 33 | KV/mm |
Comparative Tracking Index | | IEC 60112 | 600 | V |
Volume Resistivity | | IEC 62631-3-1 | 1.0E+16 | ohms·m |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 100 | °C |
Drying time - Hot air dryer | | | 6.0 到 8.0 | hr |
Suggested Max Moisture | | | 0.10 | % |
Processing (Melt) Temp | | | 325 到 335 | °C |
Mold Temperature | | | 110 到 130 | °C |
Mold Temperature | Drying Recommended | | yes | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 35 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 35 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 0.40 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 1.5 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 3.0 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 0.40 mm | IEC 60695-2-13 | 750 | °C |
Glow Wire Ignition Temperature | 1.5 mm | IEC 60695-2-13 | 800 | °C |
Glow Wire Ignition Temperature | 3.0 mm | IEC 60695-2-13 | 825 | °C |
Flame Rating | 0.40 mm | UL 94, IEC 60695-11-10, -20 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.