Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：24hr | ASTMD955 | 0.70to0.90 | % |
| Modeling Shrinkage | TD：24hr | ASTMD955 | 0.70to0.90 | % |
| Modeling Shrinkage | TD:24hr | ISO294-4 | 0.70to0.90 | % |
| Modeling Shrinkage | MD:24hr | ISO294-4 | 0.70to0.90 | % |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.40 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.46to1.4 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | ISO527-2 | 232 | Mpa |
| Tensile Strain | Break | ISO527-2 | 1.3 | % |
| Flexural Stress | | ISO178 | 425 | Mpa |
| Tensile Modulus | | ISO527-2/1 | 35500 | Mpa |
| Tensile Elongation | Break | ASTMD638 | 1.0 | % |
| Flexural Modulus | | ASTMD790 | 26800 | Mpa |
| Flexural Modulus | | ISO178 | 26600 | Mpa |
| Flexural Strength | | ASTMD790 | 441 | Mpa |
| Tensile Modulus | | ASTMD638 | 33800 | Mpa |
| Tensile Strength | Break | ASTMD638 | 261 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | >250 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | >249 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | ASTMD257 | 1.0E+2to1.0E+4 | ohms |
| Volume Resistivity | | ASTMD257 | 1.0E+2to1.0E+4 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Multi-Axial Instrumented Impact Energy | | ISO6603-2 | 5.00 | J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.3 | kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 45 | kJ/m² |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 7.00 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.