PPA AKROLOY® PA GF 60 NA AKRO-PLASTIC GERMANY

Unit Price:
$4562 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Across Flow	ISO 294-4	0.50	%
Modeling Shrinkage	Modeling Shrinkage	流量	ISO 294-4	< 0.30	%
Moisture Absorption	Saturation, 23°C	ISO 62	3.0 到 3.5	%
Spiral Flow?2,?3		内部方法	47.0	CM
Humidity Absorption - 62% RH	70°C	ISO 1110	0.80	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus		ISO 527-2/1	21000	Mpa
Flexural Modulus		ISO 178	20000	Mpa
Flexural Stress		ISO 178	405	Mpa
Tensile Stress	Break	ISO 527-2/5	275	Mpa
Tensile Strain	Break	ISO 527-2/5	2.5	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Linear thermal expansion coefficient	Flow : 23 to 80°C	ISO 11359-2	1.5E-5	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 80°C	ISO 11359-2	5.5E-5	cm/cm/°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed	ISO 75-2/B	245	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed	ISO 75-2/A	225	°C
50% Loss of Tensile Strength, 20000 hr			110 到 130	°C
50% Loss of Tensile Strength, 5000 hr			140 到 150	°C
Melting Temperature		DIN EN 11357-1	255	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Comparative Tracking Index	Solution A	IEC 60112	600	V

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	90	kJ/m²
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	100	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness	H 961/30	ISO 2039-1	330	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Glow Wire Ignition Temperature	0.8 mm	IEC 60695-2-13	650	°C
Burning Rate	1.00 mm	FMVSS 302	< 100	mm/min
Flame Rating	0.8 mm	UL 94	HB
Reinforcement Content		ISO 1172	60	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.